Environmental stress cracking

Environmental stress cracking (ESC) is a failure mechanism in polymeric materials, particularly thermoplastics, where cracks form due to the combined action of sustained tensile stress and exposure to specific environmental agents, such as chemicals, solvents, or surfactants, at stress levels well below the material's short-term yield strength.^[1] This brittle fracture occurs without significant chemical degradation of the polymer chains, distinguishing it from other forms of environmental attack.^[2] ESC is a prevalent issue in engineering applications, responsible for 25-30% of all plastic part failures, with economic impacts estimated at over £100 million annually in the UK alone (as of 2005) due to unexpected component breakdowns in industries like automotive, medical devices, and piping systems.^[3]^[1] Amorphous polymers, such as polycarbonate (PC) and acrylonitrile-butadiene-styrene (ABS), are especially susceptible because their non-crystalline structure allows easier penetration by environmental agents, while semi-crystalline materials like high-density polyethylene (HDPE) can also fail under prolonged exposure.^[2] Common triggers include household cleaners, lubricants, and even water in some cases, often exacerbated by residual molding stresses or design-induced concentrations.^[4] The underlying mechanism begins with the diffusion of the environmental agent into stressed regions of the polymer, leading to localized plasticization that weakens intermolecular forces like van der Waals bonds and hydrogen bonding.^[5] This facilitates molecular slippage and the formation of crazes—microscopic voids bridged by fibrillar material—perpendicular to the applied stress, which propagate into macroscopic cracks over time.^[2] Factors influencing ESC susceptibility include polymer molecular weight (higher weights enhance resistance), crystallinity (increased crystallinity can improve resistance in semi-crystalline polymers), and the chemical's solubility parameter matching the polymer's, which accelerates absorption.^[4] For instance, exposure of PC to acetone or ABS to surfactants can induce rapid crazing, while HDPE pipes may crack in the presence of detergents due to interlamellar failure in crystalline-amorphous interfaces.^[2]^[6] To mitigate ESC, material selection often favors higher molecular weight resins, cross-linked variants like XLPE, or blends with impact modifiers, while design practices minimize stress concentrations and compatibility testing per standards such as ASTM D1693 (bent-strip method) or ISO 22088 evaluates resistance under simulated conditions.^[4]^[3] Ongoing research emphasizes understanding tie-molecule degradation and stress relaxation to develop more robust polymers for demanding environments.^[6]

Fundamentals

Definition and Overview

Environmental stress cracking (ESC) is defined as an external or internal crack in a plastic caused by tensile stresses less than its short-term mechanical strength, in the presence of an active chemical environment.^[7] This brittle failure mode occurs in polymers under the combined influence of mechanical or residual tensile stress and exposure to specific chemical agents, resulting in crack initiation and propagation without the rupture of primary chemical bonds in the polymer structure.^[7] ESC represents a leading cause of premature failure in plastic components, accounting for approximately 25% of all such failures across various applications.^[5] It significantly impacts industries including packaging, piping systems, and consumer goods, where polymers are routinely subjected to both stress and environmental exposures, leading to unexpected brittle fractures that compromise product integrity and safety.^[5] The basic process involves the formation of crazes or microcracks at stress concentration points, such as surface defects or notches, when aggressive environmental agents like solvents or surfactants interact with the polymer.^[8] These agents facilitate localized deformation and chain disentanglement, accelerating crack growth under otherwise subcritical stress levels.^[8] Unlike pure mechanical cracking, ESC requires this environmental trigger to induce failure, distinguishing it as a synergistic phenomenon rather than a solely stress-driven process. This behavior in polymers is analogous to stress corrosion cracking observed in metals, though the underlying mechanisms differ due to the distinct material structures. Environmental stress cracking (ESC) in polymers is distinct from stress corrosion cracking (SCC) in metals, as the former primarily involves the disruption of secondary bonds and physical processes like crazing without anodic dissolution or electrochemical corrosion, whereas SCC requires a corrosive environment that leads to material loss through oxidation-reduction reactions.^[2]^[9] The term "environmental stress cracking" was coined in the 1950s specifically for plastics to differentiate this phenomenon from the corrosion-based failures observed in metals, highlighting the absence of chemical bond breaking in polymer chains during ESC.^[10] This distinction underscores that ESC exploits existing tensile stresses in conjunction with environmental agents to induce brittle failure, without the material degradation characteristic of metallic SCC.^[11] Unlike general polymer degradation, which involves chain scission or oxidative breakdown of covalent bonds often triggered by heat, UV radiation, or aggressive chemicals, ESC does not alter the polymer's molecular structure but instead accelerates mechanical failure through localized plasticization and molecular slippage under stress.^[12]^[9] In ESC, the environmental agent acts physically to reduce intermolecular forces, promoting craze formation and crack propagation without requiring high-energy inputs that degrade the backbone, thereby preserving the overall chemical integrity of the polymer while leading to premature fracture.^[2] ESC also differs from fatigue cracking, where repeated cyclic loading causes progressive damage through crack initiation and growth under purely mechanical conditions, often over extended periods at moderate stresses; in contrast, ESC demands simultaneous exposure to a chemical environment and typically occurs under static or constant stress at lower levels, resulting in faster failure times due to the synergistic environmental influence.^[9]^[2] This environmental dependency means that polymers resistant to fatigue may still succumb to ESC in susceptible media, emphasizing the role of the agent in lowering the effective stress threshold for cracking. Finally, ESC must be differentiated from pure solvent cracking, where aggressive solvents cause swelling, dissolution, or softening of the polymer without applied stress, leading to bulk material changes; ESC, however, requires concurrent tensile stress to manifest, with milder agents inducing surface-specific crazing rather than widespread plasticization or solvation.^[6]^[12] Without this stress component, the environmental agent alone may not propagate cracks, highlighting ESC as a stress-dependent failure mode rather than a simple solvational process.^[9]

Mechanisms

General Mechanisms

Environmental stress cracking (ESC) in polymers arises from the synergistic interaction between applied tensile stress and exposure to a chemical agent, leading to premature brittle failure at stress levels below the material's intrinsic yield strength. The process begins with the chemical agent contacting the polymer surface, particularly at stress concentration points such as flaws or molecular defects. Under tensile stress, polymer chains separate slightly, creating pathways for the agent to diffuse into the free volume between chains. This absorption induces local plasticization, reducing the intermolecular forces that hold the chains together and thereby lowering the surface energy required for deformation. As a result, the yield stress decreases, enabling localized molecular slippage and the initiation of microvoids or crazes—narrow bands of highly deformed material oriented perpendicular to the stress direction.^[11] The formation of crazes involves a step-by-step progression: first, stress-induced chain separation widens intermolecular spaces; second, the environmental agent absorbs into these regions, disrupting van der Waals forces and hydrogen bonds that maintain chain cohesion; third, this disruption reduces the energy barrier for chain disentanglement, promoting fibril formation where stretched polymer chains bridge the craze voids; fourth, continued stress causes fibril breakdown, enlarging voids into cracks; and finally, crack propagation occurs as stress concentrates at the crack tip, accelerating failure. In a typical craze structure, fibrils span voids with diameters on the order of 10-20 nm, providing temporary bridging until they rupture, as visualized in electron micrographs showing a ladder-like network of deformed material. This mechanism emphasizes the role of the agent in facilitating subcritical crack growth by lowering the effective fracture energy, distinct from pure mechanical cracking.^[11]^[13] Crack propagation in ESC follows a Griffith-like criterion adapted for polymers, where the environmental agent enables growth at stresses insufficient for dry conditions by reducing the surface energy term. The original Griffith theory posits that crack extension occurs when the decrease in elastic strain energy equals or exceeds the increase in surface energy. For a through-crack of length $2a in an infinite plate under uniform tensile stress \sigma, the energy release rate G is derived as G = \frac{\pi \sigma^2 a}{E} for plane stress (or adjusted by (1 - \nu^2) for plane strain, where E is Young's modulus and \nu is Poisson's ratio), balanced against twice the surface energy $2\gamma per unit advance: \frac{\pi \sigma_c^2 a}{E} = 2\gamma, yielding the critical stress \sigma_c = \sqrt{\frac{2E\gamma}{\pi a}}. In linear elastic fracture mechanics, this evolves into the stress intensity factor K_I = \sigma \sqrt{\pi a} for mode I loading, with fracture when K_I reaches the critical value K_{Ic} = \sqrt{2E\gamma}. For ESC, the agent plasticizes the crack tip zone, effectively lowering \gamma or introducing a plastic work term, allowing subcritical growth (K < K_{Ic}) via facilitated chain separation and void coalescence, as modifications to Griffith's model demonstrate for liquid environments.^[13] The response to environmental plasticization varies with polymer morphology due to differences in molecular mobility. In glassy polymers below their glass transition temperature (T_g), chains are tightly packed with limited segmental motion, making them highly susceptible to ESC as the agent rapidly increases local mobility, promoting craze initiation at low stresses. Semicrystalline polymers, with ordered crystalline regions restricting chain movement and amorphous regions allowing some mobility, exhibit greater resistance; the agent must penetrate interlamellar spaces to plasticize, often requiring higher stress or more aggressive agents to disrupt tie molecules and enable crack advance. This contrast highlights how reduced mobility in crystalline domains raises the energy threshold for deformation, delaying fibril bridging and propagation compared to the more fluid-like response in glassy matrices.^[13]^[11]

Polymer-Specific Mechanisms

In amorphous polymers such as polystyrene, environmental stress cracking (ESC) primarily manifests through rapid crazing initiated by high solvent compatibility with the disordered molecular structure. The active agent diffuses into the polymer matrix, reducing intermolecular forces and promoting the formation of microvoids that coalesce into crazes, ultimately leading to brittle fracture under sustained tensile stress.^[14]^[15] This process is exacerbated in the less-organized amorphous regions, where the chemical interaction lowers the yield stress and accelerates crack propagation compared to crystalline counterparts.^[9] In semicrystalline polymers like polyethylene, ESC mechanisms differ markedly, involving interlamellar separation and tie-chain scission that enable slower crack propagation. Under stress in the presence of an active environment, such as detergents, the agent penetrates interlamellar spaces, causing separation of crystal lamellae and scission of tie chains that bridge them, which weakens the fibrillar structure within crazes and allows gradual advancement of the crack front.^[16]^[17] In high-density polyethylene specifically, cracking often initiates and propagates along spherulite boundaries due to localized stress concentrations and differential swelling between crystalline and amorphous phases, contributing to the overall slow crack growth characteristic of these materials.^[18]^[19] The susceptibility to ESC also varies with the polymer's state relative to its glass transition temperature (Tg). Below Tg, in the glassy state, polymers exhibit brittleness that enhances ESC vulnerability, as limited chain mobility restricts plastic deformation and favors craze formation under environmental attack.^[20]^[21] Above Tg, in the rubbery state, increased ductility and chain entanglement provide greater resistance to ESC by allowing stress relaxation and reducing the propensity for localized cracking.^[22] Additives significantly modify ESC mechanisms by altering polymer morphology and environmental interactions. Fillers, such as carbon black, can reinforce the matrix but may introduce stress concentrations that accelerate cracking in polyethylene, while plasticizers enhance local mobility akin to active agents, promoting crazing by effectively lowering Tg and increasing susceptibility in rigid polymers.^[23]^[24] Antioxidants, by mitigating oxidative degradation, reduce secondary contributions to chain scission and fibril weakening during ESC in polyolefins, thereby extending crack initiation times.^[9]^[25]

Influencing Factors

The susceptibility of polymers to environmental stress cracking (ESC) is profoundly influenced by their intrinsic molecular and structural properties, which determine the material's ability to resist crack initiation and propagation under combined stress and environmental exposure. Higher molecular weight generally enhances environmental stress cracking resistance (ESCR) in polymers such as polyethylene (PE) by promoting longer chain entanglements and the formation of tie molecules that bridge crystalline and amorphous regions, thereby strengthening the network against deformation and crack growth.^[26] For instance, in high-density polyethylene (HDPE), materials with a weight-average molecular weight (Mw) exceeding 200 kg/mol exhibit significantly superior ESCR compared to those below 100 kg/mol, as the extended chains exceed the critical entanglement length required for effective load transfer.^[26] Conversely, low molecular weight HDPE, such as variants with Mw around 50-100 kg/mol, displays heightened susceptibility to ESC, with failure occurring via interlamellar crack propagation at low stress intensities due to insufficient entanglement density.^[27] Polydispersity, or the breadth of the molecular weight distribution (MWD), also plays a key role in ESCR, with broader distributions—particularly bimodal MWD—improving resistance in polyolefins by incorporating a higher fraction of long chains that bolster entanglement networks without compromising processability.^[28] In PE resins, bimodal MWD structures, often achieved through metallocene or Ziegler-Natta catalysis, yield up to 2-5 times greater ESCR lifetimes in standard tests compared to unimodal counterparts of similar average Mw, as the high-Mw tail enhances tie molecule density.^[28]^[29] Crystallinity and morphology critically modulate ESCR in semicrystalline polymers like polyolefins, where higher crystallinity levels reduce amorphous regions available for solvent penetration but generally decrease overall resistance by increasing brittleness and facilitating crack propagation. In HDPE, lower crystallinity (corresponding to lower density) typically enhances ESCR by improving ductility and tie-molecule effectiveness, though morphological defects such as large spherulites can introduce stress concentrations that promote failure.^[30]^[28] Spherulite size influences this further, with larger spherulites in low-density polyethylene (LDPE) accelerating ESC by facilitating interspherulitic boundary cracking under stress, whereas finer morphologies enhance resistance through uniform load distribution.^[31] Additives and copolymer formulations alter ESCR by modifying chain architecture and surface interactions, with comonomers like 1-hexene in PE copolymers improving resistance compared to 1-butene by introducing longer branches that lower overall density and disrupt crystalline packing, thus hindering crack advance. Short-chain branching (SCB) density, often measured as SCB per 1000 carbon atoms, further modulates ESCR in polyolefins; lower SCB enhances resistance by promoting denser tie molecules and balanced crystallinity.^[26]^[32] For example, hexene-based linear low-density polyethylene (LLDPE) demonstrates 20-50% higher ESCR in bent-strip tests than butene analogs due to reduced short-chain branching density, which minimizes localized stress risers.^[26] Antioxidants and UV stabilizers, while primarily intended for oxidative stability, can indirectly bolster ESCR by preserving molecular integrity during processing, preventing chain scission that would otherwise weaken entanglement networks; however, incompatible fillers like carbon black aggregates may reduce resistance by acting as crack initiation sites.^[33] Processing conditions introduce residual stresses and morphological anisotropies that exacerbate ESC vulnerability, as uneven cooling in injection molding or extrusion generates internal tensile stresses that amplify applied loads at potential crack sites.^[34] In blow-molded PE bottles, for instance, hoop orientation from stretching increases directional strength but renders transverse directions more prone to ESC, with residual stresses up to 10-20 MPa accelerating failure in surfactant environments by 30-50% relative to annealed samples.^[35] Annealing post-processing mitigates this by relaxing stresses and refining spherulitic structure, thereby extending ESCR lifetimes.^[35] Environmental stress cracking (ESC) is primarily triggered by chemical agents that interact with polymers under stress, with the type of agent depending on the polymer's polarity. For polar polymers such as nylons (polyamides), polar solvents like alcohols (e.g., methanol or isopropanol) are common stressors, as they promote swelling and reduce intermolecular forces, facilitating crack initiation.^[30] In contrast, non-polar polymers like polyolefins (e.g., polyethylene and polypropylene) are more susceptible to non-polar agents such as hydrocarbons (e.g., hexane or kerosene) or detergents, which can penetrate the amorphous regions and induce localized plasticization.^[36] The compatibility between the chemical agent and polymer is often assessed using Hansen solubility parameters (HSP), which quantify dispersion, polar, and hydrogen-bonding interactions; agents with HSP values closely matching the polymer's (e.g., within a relative energy difference, RED, of 1-2) exhibit higher ESC potential by enabling diffusion without full dissolution.^[37] Mechanical stress plays a critical role in ESC, but only tensile stresses—whether applied externally or residual from processing—can induce cracking, as they promote chain separation and craze formation in susceptible regions. Compressive stresses do not cause ESC, lacking the directional pull needed for void development.^[1] The magnitude of tensile stress is typically low, below the material's yield strength (e.g., 5-20 MPa for many thermoplastics), yet sufficient to accelerate failure when combined with a chemical agent; higher magnitudes shorten the time to crack initiation. Duration of exposure is also key, with long-term low-stress conditions (e.g., creep-like loading over weeks to years) more prone to ESC than short bursts, while residual stresses from molding or assembly often dominate in service failures.^[30] Temperature significantly accelerates ESC through enhanced molecular mobility and diffusion rates, following an Arrhenius-like relationship where the cracking rate increases exponentially with temperature, often doubling for every 10°C rise in many polymer-agent systems.^[38] Specific polymer-agent pairs exhibit threshold temperatures above which ESC transitions from negligible to rapid, such as around 10-20°C for polycarbonate in cyclohexanone, beyond which critical strain for cracking drops sharply.^[20] Additional environmental factors include humidity, which promotes hydrolysis in moisture-sensitive polymers like polyesters (e.g., PET), exacerbating cracking in humid conditions; pH, where high alkaline environments (e.g., NaOH solutions) destabilize polymers like PVC by altering surface chemistry; and synergistic effects from surfactants, which lower surface tension and enhance agent penetration into craze tips, dramatically reducing ESC resistance in polyolefins (e.g., reducing failure time by factors of 5-10 in surfactant-laden solutions).^[30]^[39]

Characterization and Testing

Testing Methods

Testing methods for environmental stress cracking (ESC) in polymers typically involve applying controlled tensile stress to specimens while exposing them to aggressive chemical environments, such as surfactants or detergents, to simulate service conditions and measure time to failure. These techniques are standardized to ensure reproducibility and focus on ethylene-based plastics like polyethylene, though adaptations exist for other thermoplastics.^[40] Common approaches range from simple static loading tests to more sophisticated fracture mechanics-based evaluations. The bent-strip test, standardized as ASTM D1693, is widely used to assess ESC resistance in ethylene plastics.^[40] In this method, rectangular strips of the material are bent around a standard fixture with an inside width of 11.75 mm to induce constant strain (typically resulting in 20-30% surface strain for 3 mm thick specimens) and secured in a clamp to maintain constant deformation.^[41] The clamped specimens are then immersed in a 10% Igepal CO-630 surfactant solution at 50°C, and the time until the first crack appears is recorded as an indicator of susceptibility.^[28] This test is particularly effective for ranking polyethylene grades due to its simplicity and correlation with field performance in applications like bottles and pipes.^[31] The full-notch creep test (FNCT), detailed in ISO 16770, evaluates ESC under constant load conditions, especially for high-density polyethylene (HDPE) pipes.^[42] Notched cylindrical or rectangular specimens are subjected to a tensile load (e.g., 4-7 MPa) in a 10% Igepal solution at 80°C, promoting accelerated crack initiation and propagation from the notch root.^[43] Failure time is measured until brittle fracture occurs, providing data on slow crack growth resistance relevant to long-term durability.^[44] This method distinguishes between ductile and brittle failure modes and is critical for infrastructure materials.^[45] The U-bend test, outlined in ISO 22088-5, offers a straightforward screening method for constant tensile deformation in various thermoplastics.^[46] Specimens are bent into a U-shape using a fixture or bolt to achieve a predefined strain (up to 5-10%), secured to prevent relaxation, and exposed to the test environment such as alcohols or detergents at ambient or elevated temperatures.^[47] Cracking is monitored visually over time, with the test's simplicity making it suitable for initial material qualification despite potential stress relaxation effects.^[48] Advanced methods employ fracture mechanics principles with precracked specimens to quantify ESC propagation kinetics.^[49] Compact tension or single-edge notched specimens are precracked and loaded to a specific stress intensity factor (K_I) in the presence of an aggressive medium, allowing measurement of crack growth rates via da/dt versus K_I plots to characterize subcritical crack advance.^[50] Recent post-2020 developments include in-situ microscopy techniques, such as automated optical imaging during exposure, to observe real-time craze formation and crack evolution in materials like polymethyl methacrylate.^[51] These approaches provide mechanistic insights beyond time-to-failure metrics, aiding in material optimization.^[8]

Measures of Resistance

Environmental Stress Crack Resistance (ESCR) quantifies a material's ability to withstand crack initiation and propagation under combined mechanical stress and chemical exposure, defined as the time-to-failure in a standardized test environment. This metric is typically expressed in hours, representing the duration until brittle failure occurs in a specified percentage of specimens, such as the F50 value where 50% of samples fail.^[4]^[52] Ranking scales, like those from ASTM D1693, categorize resistance using F0 (time to first failure), F10 (10% failure), F50, and F100 (complete failure), enabling comparative assessment across materials such as polyethylene grades.^[41] These values are derived from tests like the Bent Strip method, providing a basis for ranking long-term durability. The strain hardening exponent serves as a key predictor of ESC resistance, reflecting the material's capacity to redistribute local strains and inhibit crack growth during deformation. In the Hollomon power-law model, true stress (σ) relates to true plastic strain (ε) as σ = K ε^n, where K is the strength coefficient and n is the dimensionless exponent (typically 0 < n < 1 for polymers). A higher n indicates greater strain hardening, correlating with improved ESC performance by promoting uniform deformation and reducing stress concentrations that accelerate cracking.^[53] To derive n, true stress and true strain are calculated from the engineering stress-strain curve obtained in a tensile test: true strain ε = ln(1 + e) (where e is engineering strain) and true stress σ = s (1 + e) (where s is engineering stress), up to necking. These are plotted on a log-log scale (log σ vs. log ε) in the uniform plastic region post-yield, with n as the slope of the linear fit. This approach, applied to polymers like polyethylene, highlights how microstructural features influencing hardening enhance resistance to environmental-induced failure.^[54] Activation energy models capture the temperature sensitivity of ESC processes, enabling extrapolation from short-term accelerated tests to predict long-term failure times. The Arrhenius equation governs this dependence:

t_f = A \exp\left(\frac{E_a}{RT}\right)

where t_f is the time to failure, A is a material-specific pre-exponential constant, E_a is the activation energy (in J/mol) for the crack propagation mechanism, R is the universal gas constant (8.314 J/mol·K), and T is the absolute temperature (K). In ESC applications, particularly for polyethylene in surfactant environments, E_a is determined by conducting tests at multiple elevated temperatures and plotting ln(t_f) versus 1/T; the slope yields E_a / R, often ranging from 50-150 kJ/mol depending on the active agent and polymer morphology. This model assumes thermally activated diffusion or chain scission at crack tips, facilitating lifetime predictions for service conditions below test temperatures.^[55]^[38] Despite their utility, these measures face limitations from variability in sample preparation, such as inconsistencies in molding, annealing, or surface finishing, which can alter stress distributions and lead to scattered failure times across replicates.^[56] Recent ISO standard revisions in the 2020s, including the 2019 update to ISO 16770 for full-notch creep testing of polyethylene, have addressed these issues by specifying tighter controls on specimen geometry, conditioning, and environmental parameters to enhance reproducibility and inter-laboratory consistency.^[57]

Examples and Applications

Industrial Case Studies

In the 1980s, high-density polyethylene (HDPE) pipes employed in gas distribution networks suffered notable failures attributed to environmental stress cracking, resulting in leaks that compromised system integrity and prompted extensive field investigations.^[58] These incidents, analyzed by organizations like Battelle, were primarily driven by slow crack growth under combined mechanical and environmental stresses, with detergent-based solutions used in laboratory testing to replicate aggressive conditions akin to surfactants present in wastewater systems.^[58] Such failures underscored the vulnerability of early-generation HDPE formulations to brittle fracture in service environments, leading to enhanced material specifications for piping and tank applications to prevent recurrence.^[48] High-density polyethylene bottles for shampoos and detergents have historically been prone to environmental stress cracking initiated by surfactants within the product formulation, often manifesting as cracks at stress concentration points like the neck-body junction or base corners during storage or transport.^[59] This issue, first prominent in the mid-1950s with the shift to plastic packaging, accelerated under elevated temperatures and humidity—conditions simulating summer warehousing—causing brittle failures that leaked contents and necessitated redesigns in bottle geometry and resin selection.^[59] The economic repercussions include substantial costs from product recalls, inventory losses, and reformulation efforts, with industry-wide adaptations like improved bimodal HDPE grades reducing but not eliminating risks in surfactant-laden applications.^[60] Recent studies as of 2021 have highlighted concerns with recycled HDPE in detergent bottles, where lower environmental stress crack resistance compared to virgin HDPE increases failure risks due to material degradation during recycling.^[61] Environmental stress cracking in medical catheters, particularly those with polycarbonate connectors, has been documented in exposure to certain intravenous fluids, such as total parenteral nutrition (TPN) solutions and antibiotics, where the combined tensile stresses from insertion and fluid pressure induce surface crazing and eventual breach.^[62] Case studies of early catheter designs reveal that suboptimal molding led to cracking during in-use flexion, allowing bacterial ingress and infection risks in intravenous lines.^[62] The U.S. Food and Drug Administration (FDA) addresses these vulnerabilities through guidelines in ISO 10993-1 for biological evaluation, mandating compatibility testing for device materials under simulated physiological conditions to ensure resistance to stress cracking and prevent clinical complications.^[63] Such regulatory frameworks have driven material shifts toward more resistant variants like polycarbonate-based urethanes in catheter applications.^[64]

Specific Material Susceptibilities

Polyethylene (PE) exhibits notable susceptibility to environmental stress cracking when exposed to branched-chain alcohols, such as the nonionic surfactant Igepal CO-630, particularly under tensile stress.^[30] Low-density polyethylene (LDPE) is generally more prone to this failure mode compared to high-density polyethylene (HDPE) in constant-tensile-load conditions, as LDPE's lower crystallinity and higher branching allow greater deformation and earlier attainment of the yield point, facilitating crack initiation and propagation.^[6] In such scenarios, Igepal acts by reducing surface tension and promoting craze formation through tie-molecule relaxation, leading to brittle fracture at stresses below the material's inherent yield strength.^[6] Styrene acrylonitrile (SAN) copolymers demonstrate vulnerability to cracking in the presence of ketones, such as acetone, especially when subjected to residual molding stresses.^[65] This susceptibility arises from the interaction between the polar nitrile groups in the acrylonitrile component and the polar solvent molecules, which disrupt intermolecular forces and accelerate local plasticization in stressed regions, promoting craze development and eventual brittle failure.^[36] For instance, exposure to acetone can induce surface crazing in SAN components within hours under moderate strain, highlighting the role of solvent polarity in exacerbating chain disentanglement at polar sites.^[65] Polyvinyl chloride (PVC) is particularly susceptible to environmental stress cracking in highly alkaline environments, such as those encountered in concrete with a pH of 12–13 due to the presence of calcium hydroxide.^[66] This interaction leads to dehydrochlorination and chain scission at the polymer surface, reducing ductility and initiating cracks under applied stress, which has resulted in failures of PVC formwork during concrete casting where hydrostatic pressure combines with the aggressive alkaline pore solution.^[66] Studies on PVC exposed to sodium hydroxide solutions mimicking concrete alkalinity show that cracking thresholds decrease significantly at pH levels above 10, with failure times shortening as stress levels approach 20–30% of the yield stress.^[66] Nylon (polyamides), such as nylon 6 and nylon 6,6, are prone to environmental stress cracking in the presence of water or alcohols, which absorb into the amorphous regions and cause swelling.^[30] This absorption induces dimensional changes, including up to 3% by weight moisture uptake causing approximately 0.5% linear expansion, that generate internal stresses and promote craze initiation under external load, ultimately leading to cracking.^[30] For example, prolonged exposure to humid environments or alcoholic solutions can reduce the material's tensile strength by approximately 20-40% while accelerating crack growth rates, as the plasticized regions lose resistance to deformation.^[30]

Prevention Strategies

Material and Design Approaches

Material selection plays a crucial role in mitigating environmental stress cracking (ESC) in polymers, particularly polyethylene, by prioritizing grades with enhanced resistance through optimized molecular architecture. Bimodal high-density polyethylene (HDPE) resins, which feature a broad molecular weight distribution with both low- and high-molecular-weight fractions, exhibit superior ESC resistance compared to unimodal HDPE due to increased tie molecules that bridge crystalline lamellae, promoting ductility under stress. ^[67] For instance, bimodal PE-RT HDPE demonstrates a transition from ductile to brittle failure at lower stress levels than standard unimodal grades, extending time to failure beyond that of standard unimodal grades. ^[67] Copolymers such as linear low-density polyethylene (LLDPE), incorporating short-chain branches like butene or hexene, further improve ESC resistance by reducing crystallinity and enhancing interlamellar shear, with LLDPE often outperforming HDPE in constant-strain tests (e.g., >100 hours vs. 48 hours to failure). ^[4] Cross-linked polyethylene (XLPE) variants enhance resistance by forming a networked structure that limits chain mobility and crack propagation.^[4] Incorporating additives into polymer formulations can significantly bolster ESC resistance by modifying morphology and ductility. Impact modifiers, such as rubber particles (e.g., ethylene-propylene rubber or acrylic rubber), act as crack-blunting agents in matrices like polycarbonate or styrenic polymers, dispersing stress and hindering craze propagation to increase failure time under environmental exposure. ^[9] Nucleating agents, when added at controlled levels (e.g., 75-200 ppm), promote uniform crystallization in polyethylene, potentially stabilizing the microstructure to reduce stress concentration sites, though their primary benefit lies in balancing crystallinity without excessively compromising ductility. ^[68] Design principles focused on stress distribution are essential for minimizing ESC susceptibility in plastic components. Avoiding sharp corners eliminates stress risers that initiate cracks; instead, incorporating fillet radii—at least 0.5 times the wall thickness (preferably 0.6-0.75 times)—redistributes loads and improves flow during molding, as seen in guidelines for injection-molded parts. ^[69] Using thicker sections in high-stress areas further reduces residual stresses from processing, lowering the likelihood of crack initiation by promoting even load bearing across the material. ^[14] Processing optimizations during fabrication help achieve microstructures that inherently resist ESC by controlling internal stresses and crystallinity uniformity. Annealing relieves residual molding stresses, enhancing overall durability in polymers. ^[70] In extrusion processes, optimizing parameters such as cooling rates—faster cooling to limit excessive crystallinity—yields more uniform lamellar structures, improving ESC performance while maintaining mechanical integrity, as higher cooling rates can decrease crystallinity and boost resistance in blow-molded polyethylene. ^[70]

Testing and Mitigation Techniques

Accelerated aging tests are employed to predict the service life of polymeric components susceptible to environmental stress cracking (ESC) by simulating long-term exposure in a shortened timeframe, often through elevated temperatures and chemical immersion. These tests accelerate craze initiation and crack propagation by enhancing molecular mobility and environmental diffusion, allowing estimation of failure times under service conditions. A common method is the bent strip test per ASTM D1693, where notched specimens are strained and exposed to active agents like surfactants, with temperature increases (e.g., from 23°C to 50°C) reducing test duration from weeks to days while correlating to real-world aging via Arrhenius modeling.^[71] Such protocols enable service life predictions by extrapolating failure data, though validity depends on matching activation energies between lab and field exposures. In-service monitoring of ESC relies on non-destructive techniques to detect early crack formation in operational components, preventing catastrophic failure without disassembly. Acoustic emission (AE) monitoring is a prominent method, capturing transient elastic waves from microcrack initiation and propagation in stressed polymers. In polyethylene terephthalate (PET) exposed to alkaline solutions, AE signals distinguish shear banding from craze development, identifying critical stress thresholds (e.g., 45-60 MPa) for brittle fracture onset under tensile loads.^[72] Similarly, for polystyrene in fluid environments at elevated temperatures (25-55°C), AE hit rates and energy releases correlate with ESC progression, enabling real-time assessment of damage accumulation and fluid-polymer interactions. These AE systems, often integrated with sensors on pipelines or containers, provide continuous data for predictive maintenance, with signal processing algorithms filtering noise to focus on ESC-specific events like craze fibrillation.^[73] Post-manufacture mitigation strategies address ESC in deployed components by applying protective measures that interrupt environmental agent ingress or neutralize their effects. Coatings and barrier layers form impermeable shields on polymer surfaces, reducing chemical diffusion and local plasticization that drive cracking. For instance, protective coatings on polycarbonate limit aggressive agent absorption, suppressing surface softening and delaying crack initiation under tensile stress.^[74] Fluoropolymer or UV-stabilized barrier films similarly enhance resistance in machine guarding applications, extending service life in chemical-rich settings by minimizing stress concentrations at the coating-substrate interface. Chemical treatments, such as surface compatibilization or additive infusion, neutralize aggressive agents by altering wettability or chain entanglement; for example, post-cure annealing in inert atmospheres relieves residual stresses in thermosets, while topical inhibitors like siloxanes mitigate alkaline-induced hydrolysis in polyesters.^[9] These interventions are applied via spray, dip, or vapor deposition, with efficacy verified through post-treatment ESC testing to ensure adhesion and durability under cyclic loading. Standards and regulations guide the implementation of testing and mitigation for ESC, particularly in high-stakes sectors like automotive plastics, emphasizing harmonized protocols for reliability. The ISO 22088 series (Parts 1-6, established 2006) provides comprehensive methods for ESC assessment, including bent-strip and slow strain rate tests tailored to thermoplastic behaviors in chemical environments, and is widely adopted for automotive components like fuel system parts.^[75]^[76] Regulatory bodies like the SAE International reference these in J2557 for plastic fuel tank durability, mandating accelerated aging simulations to predict 15+ year lifespans.^[9] Compliance involves periodic audits and failure mode analysis, ensuring mitigation techniques align with service-specific hazards like biofuel exposure in vehicles.

References

[1]
[PDF] Environmental Stress Cracking – - The Madison Group
Environmental stress cracking (ESC) is a phenomenon in which a plastic resin is de- graded by a chemical agent while under stress, and it is the leading ...
[2]
Environmental Stress Cracking - an overview | ScienceDirect Topics
Environmental stress cracking is defined as the formation of surface fissures, known as crazing, in materials due to the combined effects of solvent exposure ...
[3]
[PDF] DEPC MPR 015 - NPL Publications
Environmental stress cracking (ESC) is the single biggest cause of failure in engineering plastics (Figure 1), accounting for approximately 30% of all failures ...
[4]
[PDF] Understanding Environmental Stress Crack Resistance (ESCR) in ...
Environmental stress cracking is a failure of the polymer material due to surface initiated micro cracks or fractures. These are caused by the combined ...
[5]
Environmental Stress Cracking ESC in Plastics - The Madison Group
Environmental stress cracking is a mechanism of fracture that results from the simultaneous and synergistic exposure of a plastic to chemical and stress.Missing: definition | Show results with:definition
[6]
UNDERSTANDING ENVIRONMENTAL STRESS CRACKING IN ...
Environmental stress cracking in polyethylene takes place because of interlamellar failure, which in turn is caused by relaxation of tie molecules.
[7]
D883 Standard Terminology Relating to Plastics - ASTM
Nov 20, 2023 · This terminology covers definitions of technical terms used in the plastics industry. Terms that are generally understood or adequately defined in other ...Missing: URL | Show results with:URL
[8]
Environmental Stress Cracking of High-Density Polyethylene ... - PMC
Failure due to breakage or disentanglement of the polymer chains as a result of the locally increasing stress in a fibril initiates the craze–crack mechanism.
[9]
[PDF] Environmental Stress Cracking - The Madison Group
Dec 29, 2023 · MANY FRACTURE MECHANISMS exist that can lead to failure of a plastic component; however, environmental stress cracking (ESC).
[10]
Environmental-Stress-Crack Resistance of Rigid Thermoplastic ...
In the late 1940s and early 1950s, Howard started to work on the ESCR phenomena of semicrystalline polyolefin materials.Missing: origin | Show results with:origin
[11]
https://doi.org/10.31399/asm.hb.v11B.a0006917
[12]
Q&A: Environmental stress cracking in polymer materials - Smithers
Environmental Stress Cracking (ESC) is cracking in a polymer from contact with a liquid or vapor and stress, without chemical degradation.
[13]
https://doi.org/10.1002/pen.23284
[14]
None
### Design Principles for Preventing Environmental Stress Cracking
[15]
On the mechanism of pressure-induced environmental stress ...
Fluids conventionally classified as “inert” exert a strong stress crazing and cracking effect on certain amorphous polymers when they are deformed in tension
[16]
Recent advances in slow crack growth modeling of polyethylene ...
Interlamellar separation is induced by a component of tension or compression parallel to the lamellar surface. An increase of the polymer molecular weight ...
[17]
[PDF] Characteristics of environmental stress cracking of PE-HD ... - OPUS
Aug 15, 2024 · In this study, its behavior with respect to environmental stress cracking, considered one of the most frequent damage mechanisms leading to.
[18]
Environmental stress cracking and morphology of polyethylene
Studies have been made of the fracture surfaces of high density polyethylene which failed by environmental stress cracking at very low stress.
[19]
ENVIRONMENTAL STRESS CRACKING OF POLYETHYLENE - TRID
ENVIRONMENTAL STRESS CRACKING OF POLYETHYLENE. MODIFICATION OF THE GRIFFITH THEORY FOR THE PRESENCE OF LIQUIDS HAS BEEN SHOWN TO EXPLAIN SOME FACETS OF THE ...
[20]
[PDF] Environmental Stress Cracking of Polymers. - DTIC
A two point bending method for use in studying the environmental stress cracking and crazing phenomena is described and demonstrated for a variety.
[21]
Effect of stress state and polymer morphology on environmental ...
Feb 5, 2003 · Environmental stress crazing or cracking (ESC), a long studied phenomenon, is the brittle failure of glassy thermoplastics, which are ...
[22]
The influence of sub-Tg annealing on environmental stress cracking ...
This phenomenon is called environmental stress cracking (ESC). Due to their loose structure, ESC is a particular problem for glassy polymers [1]. As a typical ...
[23]
Effect of Additives on Thermal Degradation and Crack Propagation ...
Jul 19, 2024 · The addition of carbon black negatively impacts stress cracking, while adding an antioxidant with a compatibilizer improved the time before ...
[24]
[PDF] Plasticizer-Induced Stress Cracking of Polycarbonate Stopcock Body
Plasticizers with lower viscosities such as DOA (Dioctyl Adipate) and ATBC. (Acetyl Tributyl Citrate) were found to more readily induce stress cracking in rigid ...
[25]
(PDF) On the Environmental Stress Cracking Resistance of High ...
Oct 11, 2020 · Finally, this research recommended a thorough investigation of the role of additives and fillers on the ESC resistant of Polyethylene.
[26]
Influence of morpho-structural parameters on environmental stress ...
Apr 15, 2025 · To optimize polyethylene's resistance to stress cracking, lamellar thickness must be carefully managed. A balance between sufficiently thick ...Missing: scission | Show results with:scission
[27]
Environmental stress cracking of low molecular weight high density ...
Polymer · Volume 22, Issue 2, February 1981, Pages 245-249. Polymer paper. Environmental stress cracking of low molecular weight high density polyethylene.
[28]
[PDF] Environmental Stress Crack Resistance of Polyethylene
This technical publication defines Environmental Stress Cracking (ESC) and Environmental Stress Cracking ... molecular weight distribution polymers, all ...
[29]
Molecular weight distribution and environmental stress cracking of ...
Molecular weight distribution and environmental stress cracking of linear polyethylene. James N. Herman,. James N. Herman. Owens-Illinois Inc., Toledo, Ohio.
[30]
Environmental Stress Cracking - an overview | ScienceDirect Topics
The definition of stress cracking according to ASTM D883 is “an external or internal crack in a plastic caused by tensile stresses less than its short-term ...
[31]
The effect of molecular composition and heterogeneity on the ...
Like most plastic materials, this group of polymers suffers from environmental stress cracking (ESC). ... polymers are morphology and molecular weight [21], [22].
[32]
Understanding environmental stress cracking in the Bell Test at the ...
Nov 8, 2023 · The average percentage variation in failure times for both grades failure times was 30%, which is similar to the unaltered Bell Test, which ...
[33]
Long-term mechanical performance of polyethylene pipe materials ...
On the other hand, by addition of carbon black masterbatch, resistance to slow crack growth in samples decreases since carbon black aggregates can act as stress ...<|separator|>
[34]
Environmental stress cracking resistance of a new copolymer of ...
Environmental stress cracking resistance (ESCR) is required in many applications where the plastics are in contact with different chemicals. This is especially ...
[35]
Influence of small fluctuating loads on environment stress cracking ...
Environmental stress cracking (ESC) is the result of a slow process induced by the continuous action of a small load around ambient temperature in an ...
[36]
Environmental stress cracking: A review - ResearchGate
Aug 7, 2025 · Environmental stress cracking: A review ... Environmental stress cracking initiation in glassy polymers. Article. Jan 1996. John Arnold.
[37]
On predicting environmental stress cracking in polymers
The solubility parameter, and in particular Hansen solubility parameters (HSP), have been shown useful to correlate polymer solution phenomena and chemical ...
[38]
Short-term ESC data for long-term predictions - Plastics Today
Arrhenius observed that when a process such as material creep, cracking, certain chemical reactions, or diffusion is driven by temperature, the process ...
[39]
[PDF] Studies of Environmental Stress Cracking of High Density ... - PRISM
Dec 19, 2013 · Stress cracking agents, i.e., surfactants in the ASP flooding in the present work, act to lower the cohesive forces between tie molecules in the ...
[40]
D1693 Standard Test Method for Environmental Stress-Cracking of ...
Oct 13, 2021 · This test method covers the determination of the susceptibility of ethylene plastics, as defined in Terminology D883, to environmental stress-cracking.
[41]
Environmental Stress-Cracking Resistance (ESCR) - ASTM D1693
ESCR testing is performed by slowly bending the test specimens and placing them in a holding clamp. The clamp and specimens are then placed in a test tube and ...
[42]
ISO 16770:2019 - Full-notch creep test (FNCT)
In stockThis document specifies a method for determining the environmental stress cracking (ESC) resistance of polyethylene (PE) materials in a defined test ...
[43]
[PDF] INTERNATIONAL STANDARD ISO 16770
Full-notch creep test (FNCT). 1 Scope. This document specifies a method for determining the environmental stress cracking (ESC) ...
[44]
Full notch creep test (FNCT) of PE-HD – Characterization and ...
Full notch creep test (FNCT) of PE-HD – Characterization and differentiation of brittle and ductile fracture behavior during environmental stress cracking (ESC).
[45]
Testing on plastic pipes (PE) ISO 16770 – Stress Cracking
Full notch creep test (FNCT) of PE-HD – Characterization and differentiation of brittle and ductile fracture behavior during environmental stress cracking (ESC).
[46]
ISO 22088-5:2006 - Plastics — Determination of resistance to ...
2–5 day deliveryISO 22088-5:2006 specifies a method for determining environmental stress cracking (ESC) of thermoplastics under constant tensile deformation, applicable to ...Missing: U- bend
[47]
[PDF] ISO 22088-5 - iTeh Standards
Aug 1, 2006 · This part of ISO 22088 specifies a method for the determination of the environmental stress cracking (ESC) behaviour of thermoplastics when they ...Missing: U- | Show results with:U-
[48]
DURABILITY: Environmental Stress Crack Resistance of HDPE
Bending the specimen into a U shape causes tensile stress on the outer radius of the bend, but stress relaxation over time reduces the tensile stress and after ...
[49]
A fracture mechanics approach to environmental stress cracking in ...
Environmental stress cracking of ... The effects of caustic concentration and polymer molecular weight on creep crack growth behaviour were determined.
[50]
A fracture mechanics approach to characterising the environmental ...
A fracture mechanics test is developed for environmental stress cracking. The method considers the contribution of both crack initiation and propagation.
[51]
Quantitative in-situ evaluation of environmental stress cracking ...
Sep 27, 2025 · High molecular weight PMMA-2 exhibits restricted polymer chain ... Gholamreza, Environmental Stress Cracking of Glassy Polymers, (2014).
[52]
https://www.testronixinstruments.com/blog/escr-environmental-stress-crack-resistance-test-guide/
[53]
[PDF] ASTM-D1693.pdf
1.1 This test method covers the determination of the sus- ceptibility of ethylene plastics, as defined in Terminology. D883, to environmental stress-cracking ...<|control11|><|separator|>
[54]
Role of an active environment of use in an environmental stress ...
The role of the environment in the overall ESC and in the ESCR tests and its interaction with the polymer have not been satisfactorily described. The role of ...Missing: variability | Show results with:variability
[55]
Strain hardening modulus as a measure of environmental stress ...
Aug 6, 2025 · In this paper it is shown that the resistance to slow crack propagation in polyethylene can be predicted from a simple tensile measurement performed at 80 8C.
[56]
Time-Temperature Strain and Molecular Weight Effects in the ...
Environmental stress cracking lifetimes of polyethylene can be described in terms of the effects of strain, molecular weight, and temperature. When these ...
[57]
Assessment of Commercially Available Polyethylene Recyclates for ...
Methods. Differences in specimen preparation, conditioning, and testing often impede objective comparisons between material data of different suppliers.
[58]
(PDF) Environmental Stress Cracking of High-Density Polyethylene ...
Oct 14, 2025 · Additionally, the limitations of linear elastic fracture mechanisms for visco-elastic polymers exposed to environmental liquids are discussed.
[59]
Environmental Stress Cracking as a Tool for Evaluating... #1982
The phenomenon of environmental stress cracking, which occurs when polyethylene is placed under stress until failure in a detergent environment, ...Missing: wastewater | Show results with:wastewater
[60]
Get a Handle on Stress-Cracking In HDPE Bottles
Aug 1, 2008 · The potential for environmental stress cracking (ESCR) of HDPE bottles has always existed because of the material's inherent semi-crystalline characteristics.<|separator|>
[61]
[PDF] Case study on detergent bottles | OECD
This case study investigates aspects of environmental sustainability and human health influenced by chemical selection for a rigid plastic packaging for liquid ...
[62]
[PDF] Feasibility of Using Plastic Pipe for Ethanol Gathering
Sep 28, 2009 · The stress then causes fracture at these weak areas. This is often termed "environmental stress cracking, ESC (or crazing if not as severe)".
[63]
Ageing properties and polymer/fuel interactions of polyamide 12 ...
Jan 4, 2019 · An analysis of environment effect on ethanol blends with plastic fuel and blend optimization using a full factorial design. Article Open ...
[64]
Environmental stress cracking of polycarbonate catheter connectors
Aug 7, 2025 · The case study shows how the first versions of one design were poorly moulded and cracked during service, allowing bacteria to enter the line and so infect the ...
[65]
[PDF] Use of International Standard ISO 10993-1, "Biological evaluation of ...
Sep 8, 2023 · This FDA guidance document, issued September 8, 2023, covers the use of ISO 10993-1 for biological evaluation of medical devices within a risk ...Missing: cracking | Show results with:cracking
[66]
[PDF] Parker Hannifin
These tubes were then kinked to create a stress riser and exposed to acid, alkaline, or saline solutions at elevated temperatures. These conditions were chosen ...
[67]
[PDF] Investigations on Environmental Stress Cracking Resistance of ...
Typical solvents that cause stress cracking in most amorphous polymers include petroleum ether, carbon tetrachloride, toluene, acetone, ethanol and chloroform.
[68]
Environmental stress cracking of poly(vinyl chloride) in alkaline ...
Aug 5, 2025 · The environmental stress cracking (ESC) effects on PVC of various high pH sodium hydroxide environments have been studied.Missing: concrete | Show results with:concrete
[69]
[PDF] Stress-Cracking Resistance of Bi-modal PE-RT HDPE Geomembrane
Bi-modal PE-RT HDPE has higher stress-cracking resistance than standard HDPE, with no clear transition from ductile to brittle failure, and a very low risk of ...
[70]
polyethylene formulations with improved barrier and environmental ...
Apr 6, 2023 · ... ESCR F50 value was 210 hours. At low nucleating agent levels, such as 75 ppm, the effect on ESCR was expected to be negligible; however, it ...
[71]
[PDF] Design guides for plastics - Tangram Technology
▫ Avoid sharp internal corners. ▫ Internal radii should be at least 0.5 and preferably 0.6 to 0.75 times the wall thickness. ▫ Keep ...
[72]
The Impact of Internal Stress and Annealing on the Oxidation ...
Jun 9, 2025 · Annealing removes internal stresses, so that physical cracking is reduced during oxidative degradation. The crack density decreased by 89.3% and 88.4% after ...
[73]
[PDF] Formolene® Polyethylene Extrusion Blow Molding Process Guide
An increase in the rate of cooling will decrease the amount of crystallinity, which can improve environmental stress crack resistance and decrease part ...<|control11|><|separator|>
[74]
[PDF] Review of accelerated ageing methods and lifetime prediction ...
The Arrhenius equation is one of the best-known models for assessing the lifetime of polymers and is commonly used to predict the combined effects of ...
[75]
https://www.iso.org/standard/34861.html
[76]
Evaluating the influence of contacting fluids on polyethylene using ...
Acoustic emission (AE) methods are proposed herein as a suitable approach to both characterize the plasticizing effect of a fluid at the time of failure (ex.
[77]
https://www.ferndalesafety.com/environmental-stress-cracking-in-machine-guarding/
[78]
ISO 22088-1:2006 - Plastics — Determination of resistance to ...
In stock 2–5 day deliveryISO 22088-1:2006 provides guidance for selecting test methods to determine environmental stress cracking (ESC) of thermoplastic materials.Missing: 22088-1:2023 | Show results with:22088-1:2023
[79]
ISO 22088-6:2006 - Plastics — Determination of resistance to ...
In stock 2–5 day deliveryISO 22088-6:2006 describes a procedure for assessing the environmental stress cracking (ESC) susceptibility of polymeric materials in chemical environments ...Missing: post- automotive