Expanded polyethylene

Expanded polyethylene (EPE) is a lightweight, closed-cell foam material manufactured from low-density polyethylene (LDPE) resin through a physical foaming process that introduces gas to create tiny, sealed cells within the structure.^[1] This results in a semi-rigid, flexible product with densities typically ranging from 20-30 kg/m³, offering superior shock absorption and resilience without permanent deformation after repeated impacts.^[1] Known for its non-abrasive, dust-free nature and recyclability, EPE is CFC-free and ozone-friendly, ensuring environmental compatibility in various uses.^[2] The material's closed-cell configuration provides key properties such as waterproofing, resistance to moisture and chemicals like acids, alkalis, and oils, as well as tear and puncture resistance.^[3] It also exhibits strong thermal insulation capabilities, with an R-value of approximately 4 per inch, and high compressive strength that supports multi-directional impact protection.^[3] These attributes make EPE durable and reusable, contributing to reduced shipping weights and lower CO₂ emissions in logistics.^[2] Common applications of EPE span protective packaging for electronics, furniture, and fragile goods; thermal and acoustic insulation in construction and automotive sectors; and specialized uses in medical positioning, military equipment, and consumer products like yoga mats.^[1] In packaging, its lightweight and cushioning qualities protect items during transit, while in automotive contexts, it serves as dunnage and padding for vibration control.^[3] The foam's versatility extends to buoyancy aids and tool control inserts, highlighting its role in industries requiring reliable, cost-effective performance.^[2]

Overview and Composition

Definition and Types

Expanded polyethylene (EPE), also known as expanded polyethylene foam, is a closed-cell foam material derived from polyethylene resin through a physical expansion process involving blowing agents. This process typically begins with impregnating polyethylene beads with a gaseous blowing agent, followed by controlled heating to expand the beads into a lightweight, semi-rigid structure characterized by a uniform cellular matrix. The resulting foam exhibits high resilience, impact absorption, and resistance to moisture and chemicals, making it suitable for various protective and insulating applications.^[4]^[5] EPE is categorized primarily by the base polymer used, which influences its mechanical and thermal characteristics. Common variants include those based on low-density polyethylene (LDPE) for enhanced flexibility, linear low-density polyethylene (LLDPE) for improved strength in blends, and high-density polyethylene (HDPE) for greater rigidity and durability. These can be formulated as homopolymers or blends, such as LLDPE with additions of LDPE or HDPE, to tailor specific performance needs during expansion.^[5]^[6] In terms of physical forms, EPE is available as expandable beads for further processing, as well as finished products like sheets, planks, rods, and custom-molded parts, allowing versatility in manufacturing. Densities typically range from 14 to 120 kg/m³, with lower densities (around 15–30 kg/m³) providing superior cushioning and higher densities offering increased structural support. Unlike other common foams such as expanded polystyrene (EPS) or polyurethane foams, EPE is polyethylene-specific, providing better flexibility, recyclability, and resistance to oils and solvents while maintaining a non-crosslinked, closed-cell architecture.^[6]^[4]

Chemical Structure

Expanded polyethylene is derived from polyethylene (PE), a thermoplastic polymer synthesized through the polymerization of ethylene monomers. The chemical structure of PE consists of long, linear or branched chains of repeating units, each comprising two carbon atoms and four hydrogen atoms, represented by the simplified formula (\ce{C2H4})_n. These chains are formed by the addition polymerization of ethylene (\ce{CH2=CH2}), resulting in a backbone of methylene groups linked as -\ce{(CH2-CH2)_n}-. This basic structure imparts PE with its characteristic non-polar, hydrophobic nature and flexibility, essential for foam applications.^[7] Variations in the PE structure arise from differences in polymerization conditions, leading to low-density polyethylene (LDPE) and high-density polyethylene (HDPE), both of which can serve as base materials for expanded polyethylene. LDPE features a highly branched chain structure due to free-radical polymerization, which reduces crystallinity and density (typically 0.910–0.940 g/cm³), enhancing flexibility. In contrast, HDPE exhibits a more linear, unbranched structure from Ziegler-Natta or metallocene catalysis, resulting in higher crystallinity and density (0.941–0.965 g/cm³), which provides greater strength. Expanded polyethylene foams are predominantly produced from LDPE or linear low-density polyethylene (LLDPE) resins to achieve the desired lightweight, resilient cellular form, though HDPE variants exist for stiffer applications.^[2]^[8] The expansion process modifies the PE structure by incorporating physical blowing agents into the polymer beads, creating a foamed morphology without altering the core chemical composition. During impregnation in an autoclave, agents such as butane, pentane, or carbon dioxide are diffused into the PE resin under elevated pressure and temperature, becoming entrapped within the polymer matrix. Upon subsequent heating and pressure release, these agents vaporize and expand, stretching the PE chains to form a network of closed, gas-filled cells surrounded by thin polymer walls. This cellular structure, typically non-crosslinked in standard expanded polyethylene, results in a material where the original PE chains maintain their integrity but are reorganized into an interconnected foam architecture with cell sizes ranging from micrometers to millimeters, enhancing volume while preserving the thermoplastic properties.^[2]^[9]^[10]^[11]

Physical and Mechanical Properties

Density and Cellular Structure

Expanded polyethylene (EPE) foam exhibits a predominantly closed-cell structure, where over 90% of the cells are sealed, typically approaching 100% in well-processed materials, which enhances its resistance to water absorption and maintains structural integrity under load.^[12] The cells are generally uniform and spherical, with diameters typically ranging from 0.25 to 0.5 mm depending on processing conditions such as expansion ratio and cross-linking.^[12]^[13] This configuration arises from the physical expansion of polyethylene beads, resulting in a semi-rigid matrix that balances lightness with mechanical resilience. Bulk density in EPE foam varies significantly to suit different applications, with low-density variants typically ranging from 14 to 30 kg/m³ for flexible forms used in cushioning, while higher densities up to 120 kg/m³ are achieved for more rigid structures requiring greater load-bearing capacity.^[14]^[15] These density levels are controlled by the degree of expansion during manufacturing, where lower densities correspond to higher expansion ratios and larger cell volumes, leading to increased compressibility and flexibility under deformation.^[12] Conversely, higher densities feature smaller, more numerous cells, reducing compressibility and enhancing stiffness for structural support. Scanning electron microscopy (SEM) analysis reveals the fine details of EPE's cellular architecture, showing thin cell walls and minimal struts that form a network capable of progressive deformation.^[12] In cross-linked variants, cells appear circular and uniformly distributed with low standard deviation in size (e.g., 320–370 μm in studied samples), while non-cross-linked foams exhibit more scattered distributions, contributing to superior energy absorption through controlled buckling of cell walls rather than brittle failure.^[12] This morphology allows the foam to dissipate impact energy effectively by elongating and collapsing cells in a predictable manner, with mechanical strength scaling with cross-linking density.^[12] EPE foam demonstrates mechanical properties suited to protective applications, including compressive strength of approximately 0.1–0.3 MPa at 10% deflection and tensile strength around 0.3 MPa, with elongation at break typically 100–200%.^[16]^[13]

Thermal and Acoustic Properties

Expanded polyethylene (EPE) exhibits low thermal conductivity, typically in the range of 0.03–0.04 W/m·K, making it an effective thermal insulator comparable to other cellular foams.^[13]^[16] This property arises from its closed-cell structure, which traps air and minimizes heat transfer through conduction. EPE maintains structural integrity across a broad temperature range, from -40°C to 85°C, allowing its use in both cryogenic and moderate heat environments without significant degradation.^[17]^[18] These thermal characteristics enable EPE's widespread application in insulation for packaging, construction, and protective gear, where it reduces heat loss or gain efficiently.^[19] In terms of acoustic properties, EPE provides notable sound absorption, particularly at mid-frequencies, with coefficients reaching up to 0.8 depending on thickness and configuration.^[20] For instance, in tests on 5 mm thick EPE, absorption coefficients were measured at 0.47 for 500 Hz and 0.44 for 1000 Hz, demonstrating effectiveness in attenuating mid-range noise.^[21] The material's cellular structure also contributes to vibration damping by dissipating mechanical energy through cell wall deformation, reducing transmitted noise and resonance in applications like automotive components and building panels.^[22] Chemically, EPE demonstrates high resistance due to its non-polar, hydrophobic nature, rendering it impermeable to water and non-absorbent even under prolonged exposure.^[23] It withstands oils and most organic solvents with minimal swelling or degradation, showing no effect from mineral, lubricating, and engine oils.^[23] Additionally, EPE maintains stability across a pH range of 2–12, resisting dilute acids and bases, which enhances its suitability for harsh environments without compromising integrity.

Production Processes

Bead Preparation and Expansion

The production of expanded polyethylene (EPE) bead foam commences with the processing of polyethylene resin, typically low-density polyethylene (LDPE), which is extruded into small cylindrical or spherical beads measuring 1–3 mm in diameter. These unexpanded beads serve as the foundational precursors for the foaming process, providing a uniform structure suitable for subsequent impregnation. The extrusion step ensures consistent bead size and composition, which is critical for controlled expansion. Following extrusion, the beads undergo impregnation with a physical blowing agent, most commonly n-pentane or isopentane. This step occurs in a pressurized vessel where the blowing agent diffuses into the polymer matrix, saturating the beads under controlled conditions to prevent premature expansion. Pentane functions as a volatile hydrocarbon that remains entrained within the beads until activated by heat and pressure release, enabling the formation of a closed-cell structure upon expansion. The impregnation process is essential for achieving the desired foam density and uniformity.^[24] The expansion of impregnated beads takes place in an autoclave, where they are heated to 100–150°C under a pressure of 10–20 bar, allowing the blowing agent to fully permeate the polymer. Subsequent rapid depressurization triggers the vaporization of the pentane, causing the beads to expand 20–50 times their original volume into low-density foam precursors with a cellular structure. This batch process yields stable expanded beads ready for storage or further processing, with expansion ratios tailored by adjusting temperature, pressure, and blowing agent content. This bead preparation and expansion methodology originated in the mid-1970s, when researchers in Europe and Japan adapted established techniques from expanded polystyrene (EPS) production to accommodate the semi-crystalline nature of polyethylene, overcoming challenges like limited gas retention to enable viable EPE manufacturing.^[24] Note that while this section details the bead foaming process, expanded polyethylene can also be produced via extrusion foaming, where LDPE resin is melted with a blowing agent and extruded into continuous foam sheets or profiles.^[25]

Molding and Cross-linking Techniques

The molding of expanded polyethylene (EPE) beads into finished foam products primarily employs steam chest molding, a process where pre-expanded beads are introduced into a mold cavity and fused together using pressurized steam to achieve the desired shape and structural integrity.^[26] This technique leverages the secondary expansion of residual blowing agent within the beads, triggered by steam at temperatures typically ranging from 100–120°C, which softens the polymer surfaces and promotes interbead bonding without fully melting the structure.^[27] The molding cycle generally lasts 1–5 minutes per part, encompassing bead filling, steam application, cooling, and ejection, with precise control over steam pressure (often 0.3–0.6 bar) to ensure uniform heating and minimize defects.^[28] Cross-linking techniques are applied post-molding or to the expanded beads to enhance the foam's dimensional stability and mechanical performance, particularly by forming covalent bonds between polymer chains. Chemical cross-linking involves incorporating peroxides such as dicumyl peroxide at concentrations of 1–3% into the bead formulation or during processing, which decomposes under heat to generate free radicals that initiate cross-linking, thereby improving elasticity by 20–50% compared to non-cross-linked EPE.^[29] Physical cross-linking, on the other hand, utilizes electron beam irradiation at doses of 5–20 Mrad, exposing the molded foam to high-energy electrons that induce cross-links without additives, resulting in similar elasticity gains while preserving the cellular structure.^[30] These methods are selected based on the desired foam resilience, with chemical approaches offering cost-effectiveness for batch production and physical methods providing uniform treatment for larger components. Quality control in EPE molding and cross-linking focuses on achieving complete cell fusion and minimizing voids to ensure product reliability and performance. Uniformity checks involve visual and microscopic inspections of bead interfaces post-molding to verify seamless fusion, often using techniques like scanning electron microscopy to detect incomplete bonding that could lead to weak spots.^[31] Void minimization is monitored through density measurements and pressure decay tests during the steam cycle, by optimizing steam distribution and cooling rates, as unfused areas or trapped air pockets compromise the foam's load-bearing capacity.^[27] Following bead preparation and expansion, these controls confirm that the final product exhibits consistent cellular integrity across varying densities.

Variants and Modifications

Copolymers

Copolymers of expanded polyethylene typically involve blending polyethylene (PE) with other polymers to tailor specific properties, such as enhanced toughness or flexibility, while maintaining the closed-cell foam structure essential for expansion processes. Common examples include PE-polystyrene (PS) blends, which leverage the rigidity of PS to improve overall mechanical resilience in foam applications. Another variant is PE blended with ethylene-vinyl acetate (EVA) copolymer to impart rubber-like elasticity to the otherwise semi-rigid PE foam.^[32] These copolymer blends yield notable performance gains over pure expanded PE, which exhibits moderate tensile strength but can display brittleness under impact. Such modifications make the foams less prone to fracture compared to base expanded PE. Production of copolymer beads for expansion requires adaptations to ensure compatibility with blowing agents. For PE-PS blends, volatile organic agents are incorporated to allow effective impregnation and expansion while accommodating the blend's viscosity. In PE-EVA systems, chemical blowing agents are used, with nanofillers aiding nucleation and gas retention to achieve finer cells and higher densities without compromising blend homogeneity.^[32]

Cross-linked Forms

Cross-linked forms of expanded polyethylene, also known as XLPE or IXPE foam, involve modifying the polymer structure through the formation of covalent bonds between molecular chains, enhancing overall durability and performance compared to non-cross-linked variants.^[6] This process transforms the thermoplastic material into a more thermoset-like structure, improving resistance to deformation and environmental stresses. Two primary types of cross-linking are employed: physical methods, such as electron beam (e-beam) irradiation, which induce uniform bonds across the foam matrix without additives; and chemical methods, utilizing agents like peroxides or silanes to create targeted covalent links between polyethylene chains.^[33]^[34] These techniques are often integrated during or after the expansion and molding stages to ensure even distribution within the cellular structure.^[35] The key effects of cross-linking include superior mechanical stability and thermal resilience, making these foams suitable for demanding applications requiring long-term shape retention. For instance, cross-linked expanded polyethylene exhibits a compression set typically below 20%.^[36] Additionally, service temperatures can reach up to 120°C in specialized formulations, compared to lower limits in standard expanded polyethylene, due to reduced chain mobility and enhanced heat resistance from the cross-linked network.^[37] These enhancements also contribute to improved chemical resistance and dimensional stability, with the foam maintaining integrity under moisture and moderate chemical exposure.^[38] In terms of market prevalence, as of 2023, the cross-linked segment accounted for USD 2 billion, representing about 61% of the global expanded polyethylene foam market valued at USD 3.3 billion.^[39] This share reflects the increasing demand for durable variants in sectors prioritizing longevity over cost.^[40]

Applications

Packaging and Cushioning

Expanded polyethylene (EPE) serves a critical role in protective packaging as inserts, void fillers, and edge protectors, where it absorbs and dissipates impact energy to prevent damage to enclosed items during handling and transportation. Its closed-cell structure allows it to deform under stress while recovering its shape, making it suitable for applications requiring reliable shock mitigation. In dynamic cushioning scenarios, such as drop tests, EPE foam demonstrates effective energy absorption; for instance, increasing foam thickness from 40 mm to 60 mm at a 400 mm drop height reduces maximum acceleration from 211.5 m/s² to 150.3 m/s² under 5.63 kPa static stress, thereby lowering transmitted forces to packaged goods.^[41]^[42] Common applications include shipping electronics like computers and televisions, fragile goods such as glassware and ceramics, and medical devices including surgical instruments and diagnostic equipment, where EPE's resilience protects against multiple impacts without compromising item integrity. In these contexts, EPE often replaces expanded polystyrene (EPS) due to its superior flexibility and resistance to cracking, offering enhanced performance in scenarios involving repeated handling or irregular shapes.^[41]^[43] Key advantages of EPE in packaging stem from its lightweight construction, with typical densities around 18-30 kg/m³, which minimizes overall package weight and associated shipping costs while maintaining high strength-to-weight ratios for efficient material use. Additionally, its smooth, non-abrasive surface prevents surface scratches on delicate items, ensuring safe contact with polished or sensitive materials like painted electronics or medical tools. The closed-cell mechanical properties of EPE, including high resilience and elasticity, underpin its effectiveness as a cushioning material by converting kinetic energy into deformation without permanent damage.^[41]^[3]^[42]

Insulation and Protective Uses

Expanded polyethylene (EPE) foam is widely utilized in thermal insulation applications due to its closed-cell structure, which provides effective resistance to heat transfer and moisture ingress. In building construction, EPE sheets and boards are employed as insulation in walls, roofs, and floors to minimize energy loss, offering an R-value of approximately 4 per inch of thickness, comparable to other rigid foam insulations.^[13] For pipe insulation, EPE tubes and wraps are commonly applied to hot and cold water lines, HVAC systems, and refrigeration pipes to prevent condensation and maintain temperature, with the material's low thermal conductivity (around 0.27 Btu·in/(h·ft²·°F)), enabling efficient performance in demanding environments.^[44] This makes EPE a preferred choice for both residential and commercial installations where durability and ease of installation are essential. In protective gear, EPE serves as a key component in waterproof linings for outdoor apparel, particularly in winter clothing designed for extreme conditions. Since the early 2020s, expanded polyethylene membranes have been integrated into products like GORE-TEX ePE laminates, providing durable waterproofing, windproofing, and breathability without perfluorinated chemicals, as seen in jackets and pants from brands such as Patagonia and Gore.^[45] These membranes bond directly to fabric shells, repelling water while allowing vapor escape, enhancing comfort in alpine and snow gear launched in 2022 and expanded thereafter.^[46] Additionally, EPE foam contributes to vibration isolation in automotive parts, such as underbody panels and engine mounts, where its resilient structure absorbs shocks and reduces noise transmission during vehicle operation.^[47] Beyond insulation and apparel, EPE finds applications in acoustic barriers, flotation devices, chemically resistant seals, medical positioning aids, military equipment padding, and consumer products such as yoga mats and tool control inserts. For sound control, EPE panels, like those in the Stratocell Whisper series, are used in studios, theaters, and industrial settings to absorb and block noise due to their porous yet closed-cell design, which dampens vibrations effectively.^[22] In marine and recreational contexts, EPE's high buoyancy and water resistance make it ideal for flotation devices, including life vests and dock floats, where it maintains structural integrity under prolonged exposure to moisture.^[48] Furthermore, EPE gaskets and seals leverage the material's broad chemical resistance to solvents, acids, and bases, protecting equipment in industrial processes from corrosion and leaks. In medical applications, EPE provides positioning supports for patients during procedures, while in military uses, it offers protective padding for gear and equipment. Consumer products like yoga mats benefit from its cushioning and durability, and tool control inserts use EPE for organizing tools in cases with secure, non-slip holds.^[49]^[1]^[2]

History and Environmental Considerations

Development Timeline

Expanded polyethylene (EPE), a closed-cell foam derived from polyethylene resin, was developed in the mid-1970s through adaptations of expanded polystyrene (EPS) bead foaming techniques, with parallel innovations occurring in Europe and Japan.^[24] Early patents, such as US Patent 3,959,189 granted in 1976, detailed processes for producing foamable polyethylene resin particles via suspension polymerization and impregnation with blowing agents like hydrocarbons.^[50] This marked the initial steps toward scalable bead expansion, building on EPS methods but tailored to polyethylene's flexibility and shock-absorption properties for applications like packaging.^[51] Commercial production of EPE began in the late 1970s, with initial manufacturing facilities established in Japan and Europe around 1975–1980, focusing on non-crosslinked forms for cushioning and insulation.^[24] By the early 1980s, advancements in cross-linking expanded EPE's durability and heat resistance; for instance, US Patent 4,366,263 filed in 1980 described methods for producing expanded cross-linked polyethylene particles using chemical agents like peroxides during bead preparation. These developments enabled broader adoption in automotive and protective gear, with steam-chest molding processes refined through patents like US 4,440,703 in 1984. In the post-2000 era, EPE saw increased emphasis on recyclable variants, driven by rising demand for sustainable materials in packaging and consumer goods, though detailed global consumption data remains limited beyond early estimates from around 2001.^[24] A notable milestone occurred in the 2020s with the commercialization of expanded polyethylene membranes for waterproofing, such as Gore-Tex's ePE technology introduced in 2022, which provided per- and polyfluoroalkyl substances (PFAS)-free alternatives for outdoor apparel and was adopted by brands like Patagonia.^[52] This innovation highlighted EPE's evolving role in eco-friendly applications, leveraging its inherent recyclability and low environmental footprint.^[46]

Sustainability and Recyclability

Expanded polyethylene (EPE) is classified under resin identification code 4 as a low-density polyethylene material, facilitating its sorting in recycling streams alongside low-density polyethylene (LDPE) products.^[53] This compatibility supports mechanical recycling processes, where post-consumer or post-industrial EPE foam is densified, melted, and repurposed into lower-grade applications such as construction fillers, acoustic panels, or non-woven fabrics, though challenges like contamination from adhesives or dirt can limit efficiency.^[54] Emerging chemical recycling technologies, particularly those developed after 2020, offer promising alternatives by depolymerizing EPE into its ethylene monomers through pyrolysis or gasification, enabling the production of virgin-quality resin and reducing reliance on fossil feedstocks.^[55] The global market for mechanical and chemical polyethylene recycling, including EPE, reached USD 17.24 billion in 2024 and is projected to grow at a compound annual rate of 10.25% through 2030, driven by regulatory pressures and technological advancements.^[56] Regulatory frameworks, such as the EU Single-Use Plastics Directive (Directive (EU) 2019/904, amended through 2024), promote recyclable alternatives like EPE in packaging to reduce plastic waste.^[57] EPE exhibits a relatively low environmental footprint during use, with minimal volatile organic compound (VOC) emissions compared to solvent-based foams, contributing to better indoor air quality in applications like packaging.^[58] The shift toward environmentally friendlier blowing agents, such as carbon dioxide (CO₂) over traditional hydrocarbons like isobutane, has reduced ozone depletion potential and global warming contributions, aligning with broader industry transitions to sustainable foaming processes noted since the early 2000s.^[59] However, EPE's inherent biodegradability is limited due to its stable polyethylene structure, which resists microbial breakdown in natural environments; ongoing research into compostable additives, such as pro-oxidant formulations or bio-based modifiers, aims to enhance degradation rates in industrial composting facilities without compromising material performance.^[60] In comparison to expanded polystyrene (EPS) foams, EPE demonstrates superior recyclability, as its non-styrene composition avoids the brittleness and contamination issues that hinder EPS recovery rates, which often fall below 15% globally.^[43] EPE's broader acceptance in mechanical recycling programs positions it as a more circular option for foam-based products. Global consumption of EPE has expanded significantly, with the market valued at approximately USD 3.3 billion in 2023—reflecting an estimated volume growth to around 200,000 metric tons annually by the mid-2020s, up from earlier decades—underscoring the need for enhanced end-of-life management to mitigate landfill accumulation.^[39]

References

[1]
What is EPE Foam? Everything You Should Know
EPE stands for Expanded Polyethylene. It is a lightweight, flexible, and semi-rigid closed-cell foam made from low-density polyethylene (LDPE) resin. The ...
[2]
Know Your Foam: Polyethylene [EPE] Foam
Apr 17, 2024 · Polyethylene foam is a closed-cell foam has a number of outstanding characteristics, including water resistance, shock and vibration absorption, flexibility, ...Missing: properties applications
[3]
Expanded Polyethylene Foam (EPE)
Aug 25, 2020 · Expanded polyethylene foam, also known as EPE, is a molded semi-rigid, non-crosslinked, closed-cell polyethylene foam that is often denser and stronger.Missing: definition | Show results with:definition
[4]
https://www.ncbi.nlm.nih.gov/pmc/articles/PMC10489951/
[5]
Formation and Characterization of Polyethylene Blends for ...
Aug 7, 2025 · Blends of low density polyethylene (LDPE) and linear low density polyethylene (LLDPE) are widely used for blown film applications.
[6]
Types, Products, Properties & the Process of Polyethylene Foam
Both low-density polyethylene (LDPE) and high-density polyethylene (HDPE) are preferred, depending on the desirable end-use properties.Polyethylene Resins · Foam Extrusion · Polyethylene Foam InsulationMissing: definition | Show results with:definition
[7]
Polyethylene (PE) - EdTech Books
The functional group (X in Figure 7.1) is simply hydrogen. PE is the simplest of all polymers, with just two carbons and four hydrogens in the basic polymer ...
[8]
EPE Foams - Neostik Tapes
EPE foam, or Expanded Polyethylene foam, is a lightweight, closed-cell foam material that is known for its excellent cushioning and shock-absorbing properties.Missing: definition | Show results with:definition
[9]
Technical Data - Arplank Direct
ARPAK® Expanded Polyethylene (EPE) Products are produced using inert gas blowing agents. No VOCs are employed in the production of any ARPAK® EPE Products.
[10]
The working principle and advantage of EPE foam machine
Oct 10, 2022 · Currently, the most common foaming is using butane gas foaming. The principle of foaming is to use butane gas to be liquid in the jar, and then ...
[11]
Foamed Product - an overview | ScienceDirect Topics
Blowing agents used include methyl chloride, propylene, or butylene. A wide ... expanded polyethylene or polypropylene (EPE and EPP, respectively).Foaming · Polymeric Foam Materials For... · 10.2 Foams Classification...
[12]
[PDF] Study on Cellular Structure and Mechanical Property of Foaming ...
The cellular structure is the most crucial and decisive property for polyethylene foam material application[4]. However, cellular structure is closely related ...Missing: scientific | Show results with:scientific
[13]
[PDF] Expanded Polyethylene Foam Product Data Sheet
Physical Properties. Tensile Strength. Kg/cm2. 2.5 – 3.4. Elongation. %. 125. Compression 10%. Kg/cm2. 0.030. Compression 20%.Missing: scientific | Show results with:scientific
[14]
How to calculate the density of EPE product?
The density range of commonly used EPE product is 18~28kg/m³, but there are high density of EPE product such as 35kg/m³, 64kg/m³, 96kg/m³. In general, if the ...
[15]
High Density Poly Ethylene Foam Manufacturer, HDPE Foam Supplier
'PROTEC armour' is non-cross linked, expanded polyethylene foam (EPE / PE) of a closed-cell structure. ... These have 25 kg/m3 to 330 Kg/m3 density range.
[16]
Expanded Polyethylene Datasheet | Foam Factory, Inc.
Thermal Conductivity (K), ASTM C177, 0.30. Thermal Resistance @ 70F (R), ASTM C177, 3.3. Coeff. of Lin. Thermal Expansion (in/in/°F x 10^-5), ASTM D696, 4.0.
[17]
EPE - Product Data Sheet - Google Docs
Properties of Expanded Polyethylene Foam (EPE) ; Density. Kg/m3. 18 – 25 ; Cell Size. mm. 0.25 – 0.35 ; Tensile Strength. Mpa. 0.02 ; Elongation. %. 130 – 140.
[18]
Expanded Polyethylene Foam - EPE
... Thermal conductivity=0.025 KCal/M.hr C. Some of the salient features of our Expanded polyethylene foam are: Easy to Lay; Available with Alu Foil facing ...
[19]
EPP/EPE Foam Technical Data - foamsearch.com
EPP/EPE Foam Technical Data ; Thermal Conductivity, ASTM-C177, (K) BTU-in/ ft-hr-f, 0.26, 0.26 ; Thermal Resistance, ASTM-C178, (R) @ 70 F · 3.9, 4 ...
[20]
Polyethylene insulation Soundproofing Foam
Excellent Sound blocking properties: has a Sound Transmission Coefficient, (STC) value of 65 and a Noise Reduction Coefficient (NRC) value of 0.85 which makes ...Missing: EPE | Show results with:EPE
[21]
[PDF] MEASUREMENT OF SOUND ABSORPTION COEFFICIENTS OF ...
Equivalence of absorption coefficients for expanded polyethylene. Freq. [Hz]. Sound. Abs. Coef. Equivalent sound absorption materials and frequencies. 125. 0,03.
[22]
Stratocell Whisper | Sound absorbing closed cell PE foam panel
Stratocell Whisper is a range of closed-cell semi-rigid sound-absorbing expanded polyethylene sheets. Its sound-absorbing properties make it one of the most ...
[23]
None
### Chemical Resistance Summary for Expanded Polyethylene (EPE)
[24]
Progress in the development of bead foams – A review
Apr 25, 2022 · The usage of pentane as entrapped blowing agent for these expandable beads allows storage of the unfoamed material for several weeks or even ...
[25]
Steam-chest molding of expanded thermoplastic polyurethane bead ...
Dec 31, 2017 · Steam-chest molding uses steam to induce interbead bonding, creating molded bead foams with complex shapes. ETPU foams have high tensile ...
[26]
US20230382023A1 - Expanded Foam Product Molding Process ...
... expanded polyethylene (EPE) foam. In current EPP ... [0005]. The steam chest molding process is used to ... The temperature differential from inlet temperature to ...
[27]
Expanded beads of polyethylene moldable at low steam pressure
May 23, 2024 · Isobutane served as the blowing agent in this process, leading to the production of what we will refer to as ePE 1, ePE 2, and ePE 3.Missing: incorporation | Show results with:incorporation
[28]
Study on the foaming of crosslinked polyethylene - ResearchGate
Aug 6, 2025 · ... chemical cross-linking. Azodicarbonamide (ADCA) and dicumyl peroxide ... expanded polyethylene (EPE) foam. In field explosion ...
[29]
Promoting polyethylene foams by irradiation crosslinking in Mexico
Comparison between crosslinking of LDPE by gamma, ray from a cobalt-60 source and by electron beam was studied. Post crosslinkmg of expanded polyethylene ...Missing: peroxides | Show results with:peroxides
[30]
Evaluation of the Fusion Quality of Bead Foams Made from ...
Aug 2, 2022 · ... expanded polyethylene (EPE)), and polypropylene (as expanded ... steam chest molding process are expected to be more suitable.
[31]
An insight into simultaneous phase transition phenomena and melt-rheology of low-density polyethylene/ethylene–vinyl acetate copolymer/expanded graphite nanocomposites through continuous extrusion foaming process
### Summary of PE/EVA Blend Foams from https://www.sciencedirect.com/science/article/abs/pii/S0014305722007339
[32]
Polyethylene (PE) Crosslinking Technology - Knowledge - IFAN
Oct 20, 2023 · There are two types of crosslinking methods for polyethylene: physical crosslinking (radiation crosslinking) and chemical crosslinking. Chemical ...
[33]
Effect of the cross-linking agent on the cross-linking degree and ...
There are five main cross-linking methods for polyethylene: peroxide cross-linking, silane cross-linking, UV cross-linking, salt cross-linking and high-energy ...<|control11|><|separator|>
[34]
XPE foam VS EPE foam - Cyg Tefa
Mar 24, 2022 · Compared with EPE foam, XPE and IXPE foam materials have better mechanical properties, are stronger, more durable, and have excellent moisture- ...
[35]
Technical Data Sheet: 4# Crosslinked Polyethylene Foam - lamatek
Compression Set. ASTM D3575. %. 16. Thermal Stability. ASTM C177. % of chg @ 158 ... Working Temperature Range. °F. -70 to 175. Water Absorption. Lb/ft/°F. < 0.05.
[36]
XLPE Foam | Cross linked polyethylene foam manufacturer - Cyg Tefa
Thermal conductivity: 0.040~0.095w/m.k. Working temperature (-40℃~80℃, up to 120℃ for special specifications). Function: Thermal insulation, Waterproof and ...Missing: service | Show results with:service
[37]
Cross-Linked Polyethylene - an overview | ScienceDirect Topics
The cross-links introduced cause the high-temperature properties of the polymer to be improved, its flow is reduced, and its chemical resistance is enhanced.
[38]
Expanded Polyethylene Foam Market Size & Share Report - 2032
Cross-linked EPE foam is used in the building of energy-efficient structures, where it helps to reduce heat loss, providing superior thermal insulation ...
[39]
Polyethylene (PE) Foams Market, Industry Size Forecast [Latest]
Sep 2, 2025 · Non-XLPE foam type accounted for the largest share of the Polyethylene foams market. Non-XLPE foam is also known as non-cross-linked ...
[40]
Analysis of the Dynamic Cushioning Property of Expanded ... - NIH
Aug 30, 2023 · Expanded polyethylene (EPE) is a low-density, semi-rigid, closed-cell structure of plastic foam with a lightweight, soft surface and resistance ...Missing: definition | Show results with:definition
[41]
[PDF] PERFORMANCE OF EXPANDED POLYMER CUSHION ...
This function of foam makes it extremely useful in packaging as a cushioning material designed to protect against shock.
[42]
POLYETHYLENE VS POLYSTYRENE - EPE USA
Polyethylene proves to be a better packaging material than polystyrene even when discussing the basics of cushioning performance. Expanded polyethylene foam is ...
[43]
https://www.epeusa.com/blogs/news/polyethylene-vs-polystyrene
[44]
Next-Gen GORE-TEX Products
Waterproof. Windproof. Breathable. GORE‑TEX products with ePE membrane offer durable performance that stands the test of time.United Kingdom · Australia / New Zealand · 차세대 고어텍스 제품Missing: apparel vibration automotive
[45]
Expanded polyethylene (ePE) - Patagonia
Expanded polyethylene (ePE) is a strong, yet lightweight material that helps make gear durably waterproof without using perfluorinated chemicals.Missing: vibration automotive
[46]
The Best Types of Foam That Reduce Noise, Vibration, and Harshness
Jun 28, 2024 · Polyethylene foam is often used in packaging, construction, and automotive industries. ... applications where vibration reduction is essential.
[47]
EPE Buoyancy Foam Sheets – Lightweight, Durable & Waterproof
Apr 21, 2025 · EPE Buoyancy Foam is a closed-cell, lightweight foam designed for superior buoyancy, impact resistance, and water resistance.
[48]
[PDF] Chemical Resistance of EPE/EPP Foam
These materials are resistant to a broad spectrum of solvents and chemicals. The data presented here was supplied by our base resin material supplier and ...
[49]
https://cretexseals.com/wp-content/uploads/2023/12/chemical-resistance.pdf
[50]
Expanded Polyethylene Bead Foam Technology | Request PDF
This chapter provides an overview of expanded polyethylene (EPE) bead foam technology. The background and history of EPE production are provided.
[51]
GORE-TEX Reveals New ePE Membrane: Patagonia, Arc'teryx, and ...
Sep 21, 2022 · GORE-TEX Expanded Polyethylene debuts for fall 2022, promising long-lasting durability, a lower carbon footprint, and lighter weight.
[52]
Resin Identification Code: The Ultimate Guide - Epsole
Jul 2, 2025 · Resin Identification Code 2 (HDPE or PE-HD) HDPE is also widely accepted in recycling programs and is considered a safe and stable plastic. ...
[53]
Why Recycling Expanded Polyethylene and Expanded ...
In 1988, The Society of the Plastics Industry (SPI), now known as the Plastics Industry Association, created the Resin Identification Code (RIC) system.
[54]
Recent developments in recycling of post-consumer polyethylene ...
Mar 18, 2025 · This paper discusses advanced technologies for waste polyethylene recycling from the perspectives of green chemical reaction, high-efficiency catalytic process ...
[55]
Mechanical & Chemical Recycling Of Polyethylene Market 2030
The global mechanical & chemical recycling of polyethylene market size was valued at USD 17.24 billion in 2024 and is expected to expand at a CAGR of 10.25% ...
[56]
Expanded Polyethylene Circularity Potentials - ResearchGate
EPE has been used as packaging, insulation material, and for the production of toys and food/fruit preservation , among others. Recycling of EPE is an important ...<|control11|><|separator|>
[57]
7 Reasons CO2 is a Better Extrusion Foaming Agent - Messer
May 10, 2017 · Hydrofluorocarbons such as pentane or isobutene typically have been the foaming agent of choice for making high or low-density extruded ...
[58]
Biodegradable Polymer Materials Based on Polyethylene and ... - NIH
Jun 16, 2022 · In this paper, we consider the possibility of solving this problem by the development of biodegradable compositions based on polyolefins and elastomers.