Fatigue testing

Fatigue testing is a specialized procedure in materials science and engineering that evaluates the durability and endurance of materials and components by subjecting them to repeated cyclic loading or fluctuating stresses, typically below the material's yield strength, to determine the number of cycles to failure and identify potential crack initiation and propagation.^[1] This process simulates real-world conditions where structures experience ongoing mechanical stresses, such as in aircraft components or bridges, allowing engineers to predict fatigue life and prevent catastrophic failures.^[2] The testing typically involves three stages: crack nucleation or initiation, crack propagation through the material, and final fracture, with failure often occurring at stress levels that would not cause immediate static failure.^[3] Key methods include high-cycle fatigue testing, which focuses on elastic deformation and generates S-N curves (stress amplitude versus number of cycles to failure), often revealing an endurance limit in materials like steel below which infinite cycles cause no failure; and low-cycle fatigue testing, which accounts for plastic deformation using strain-life approaches.^[3]^[2] Standardized protocols, such as ASTM E606/E606M for strain-controlled uniaxial testing on homogeneous metallic specimens and ISO 12107:2012 for statistical planning and data analysis in low-cycle fatigue testing to ensure reliable fatigue property determination with minimal specimens, guide these evaluations.^[4] Fatigue testing is critical across industries like aerospace, automotive, and renewable energy, where components may endure millions of cycles—such as wind turbine blades, which face on the order of 10^8 load cycles over their typical 20-year service life—enabling the design of safer, more reliable systems by quantifying factors like mean stress, stress amplitude, and environmental influences such as corrosion.^[2]^[5] Common specimen types include cylindrical or flat geometries for uniform loading, with notched variants to simulate defects, and tests conducted at frequencies of 1–20 Hz using axial, bending, or torsional setups.^[4]^[1]

Fundamentals of Fatigue

Definition and Mechanisms

Fatigue in materials science refers to the progressive and localized structural damage that occurs when a material is subjected to cyclic loading, typically at stress levels below its yield strength, ultimately leading to crack initiation, propagation, and sudden fracture.^[3] This failure mode is distinct from monotonic loading because the repeated application of stress causes irreversible microstructural changes, even though each cycle may remain elastic on a macroscopic scale. Fatigue accounts for approximately 80-90% of mechanical failures in engineered components, highlighting its significance in design and reliability.^[6] The fatigue failure process unfolds in three primary stages: crack initiation, propagation, and final fracture. During crack initiation, microscopic damage accumulates through the formation of slip bands due to localized plastic deformation, where persistent slip bands (PSBs) emerge as ladder-like structures of high dislocation density that extrude or intrude the surface, serving as nucleation sites for microcracks.^[7] In the propagation stage, these microcracks grow incrementally under cyclic loading, often described by Paris' law, which relates the crack growth rate per cycle \frac{da}{dN} to the stress intensity factor range \Delta K via the empirical relation \frac{da}{dN} = C (\Delta K)^m, where C and m are material constants, and \Delta K = K_{\max} - K_{\min} quantifies the cyclic stress field at the crack tip driving subcritical extension. Final fracture occurs rapidly once the crack reaches a critical size, transitioning to unstable ductile or brittle failure.^[8] Several factors influence these mechanisms, including mean stress and the stress ratio R = \sigma_{\min}/\sigma_{\max}, where higher mean stresses or positive [R](/page/R) ratios accelerate damage by increasing the effective stress range and promoting crack opening.^[9] Environmental effects, such as corrosion fatigue, exacerbate the process by combining mechanical cycling with electrochemical reactions that dissolve protective oxide layers, initiate pits as stress concentrators, and enhance crack propagation through mechanisms like hydrogen embrittlement.^[10] At the microstructural level, crack nucleation is governed by dislocations, grain boundaries, and inclusions. Dislocations accumulate and tangle under cyclic straining, forming PSBs that concentrate shear stress and lead to microcrack formation at favorable sites.^[11] Grain boundaries act as barriers to slip, causing stress concentrations and intergranular cracking, particularly in high-cycle fatigue where transgranular paths dominate in the interior.^[12] Inclusions, such as non-metallic particles, serve as heterogeneous nucleation points by creating local stress risers and decohesion under alternating loads.^[13]

S-N Curves and Fatigue Life

The S-N curve, also known as the Wöhler curve, graphically represents the fatigue behavior of a material by plotting the stress amplitude S (typically alternating stress) against the number of cycles to failure N.^[3] This empirical relationship is derived from constant-amplitude fatigue tests and is fundamental for predicting fatigue life in engineering designs.^[14] In high-cycle fatigue (HCF), which occurs above approximately $10^4 cycles and involves primarily elastic deformation, the S-N curve exhibits a downward slope on a semi-logarithmic scale, indicating that higher stress amplitudes lead to shorter lives.^[3] Conversely, low-cycle fatigue (LCF) below $10^4 cycles is dominated by plastic deformation, where the curve steepens due to rapid damage accumulation from larger strains.^[15] For HCF, Basquin's law provides a mathematical model for the linear portion of the S-N curve on a log-log plot:

\sigma_a = \sigma_f' (2N_f)^b

where \sigma_a is the stress amplitude, \sigma_f' is the fatigue strength coefficient (often close to the ultimate tensile strength), b is the fatigue strength exponent (typically negative, ranging from -0.05 to -0.12 for metals), and N_f is the number of cycles to failure.^[16] This equation originates from the 1910 work of O.H. Basquin, who observed that plotting \log \sigma_a versus \log N_f yields a straight line, allowing extrapolation of fatigue life from experimental data.^[17] The factor of 2 accounts for the reversal in fully reversed loading (stress ratio R = -1).^[14] Many ferrous materials, such as steels, display an endurance limit on the S-N curve, represented as a horizontal asymptote at high cycle counts (typically beyond $10^6 to $10^7 cycles), below which the material can endure an infinite number of cycles without failure.^[18] This knee point marks the transition to infinite life, with the endurance limit often approximating 50% of the material's ultimate tensile strength for steels with ultimate strengths below 1400 MPa.^[19] Non-ferrous materials like aluminum alloys lack a distinct endurance limit, showing continued slope even at high cycles.^[3] Factors such as surface finish, specimen size, and temperature significantly alter the S-N curve's shape and position. Poor surface finish, like roughness from machining, introduces stress concentrations that reduce fatigue life, particularly in HCF, by accelerating crack initiation.^[20] Larger specimen sizes lower the apparent fatigue strength due to a higher probability of defects, following statistical size effects that shift the curve downward.^[21] Elevated temperatures decrease the endurance limit and steepen the curve; for example, certain alloy steels experience a 10% drop in fatigue strength at 200°C and 20% at 400°C compared to room temperature.^[21] Fatigue data exhibit inherent scatter due to material variability, microstructure, and test conditions, often modeled using the Weibull distribution to describe the probabilistic nature of cycles to failure at a given stress level.^[22] The two-parameter Weibull form is commonly applied in log-space for S-N analysis, enabling designers to incorporate safety factors based on reliability percentiles (e.g., 99% survival probability).^[23]

Test Preparation and Configurations

Specimen Types and Preparation

In fatigue testing, specimens, often referred to as coupons, are designed to represent material behavior under cyclic loading while ensuring reproducibility and standardization. Smooth bar specimens are commonly used to generate baseline S-N curves, which plot stress amplitude against cycles to failure, as they provide uniform stress distribution without stress raisers. These are typically cylindrical or rectangular in cross-section, with diameters or thicknesses ranging from 6 to 12.5 mm for axial loading, per ASTM E466 guidelines for force-controlled constant-amplitude tests. Notched specimens, in contrast, incorporate geometric features such as circumferential notches or holes to simulate stress concentration effects, quantified by the stress concentration factor K_t, which can reduce fatigue life by accelerating crack initiation at the notch root. For evaluating fatigue crack growth, specific geometries are standardized to facilitate mode I (tensile opening) loading and precise crack length measurement. The compact tension (CT) specimen is widely adopted for its compact size and ease of gripping, featuring a width W of 50 mm and thickness B of 10 mm as a standard configuration, allowing proportional scaling based on material yield strength.^[24] Center-cracked tension (CCT) specimens, with a central through-crack, are used for uniform stress fields across the crack plane, typically with widths of 100-200 mm to accommodate crack propagation. Single-edge notched (SEN) specimens mimic edge cracks in components, often with a width of 50 mm and initial notch depth of 5-10 mm, enabling simulation of boundary effects in structures. These geometries are detailed in ASTM E647 for measuring crack growth rates da/dN as a function of stress-intensity factor range \Delta K.^[24] Specimen preparation is critical to minimize artifacts that could influence results, beginning with precision machining to achieve the required geometry and surface finish, typically using CNC lathes or mills to tolerances of ±0.01 mm. Polishing follows, often with abrasive papers up to 1200 grit or electropolishing, to eliminate machining-induced surface defects like microcracks or residual stresses that serve as initiation sites, thereby isolating intrinsic material fatigue properties. Heat treatment is applied post-machining to replicate service conditions, such as annealing or aging for alloys, ensuring microstructural consistency without altering dimensions. Grip interfaces are designed with tapered or threaded ends to prevent slippage and misalignment, which could introduce bending moments and skew stress uniformity during testing.^[25] While coupon-level testing provides fundamental data, scaling results to full-scale components introduces challenges due to differences in stress gradients; uniform stress in small specimens contrasts with the steep gradients in larger structures, where peak stresses at surfaces drive initiation but decay inward, often leading to conservative life predictions if not accounted for in models. This representativeness issue underscores the need for validation through sub-component tests to bridge lab data to service environments.^[25]

Loading Protocols

Loading protocols in fatigue testing define the cyclic stress or strain patterns applied to specimens to replicate or accelerate real-world service conditions, enabling the assessment of material durability under repeated loading. These protocols vary from simple constant amplitude cycles to complex variable and spectrum sequences that account for irregular operational demands, ensuring that test outcomes align with parameters like those used in S-N curve development for baseline fatigue life prediction.^[26] Constant amplitude loading applies uniform cyclic stress or strain at a fixed maximum and minimum level throughout the test, typically using a sinusoidal waveform to simulate smooth oscillations. This approach isolates the material's response to repetitive loading without variability, with test frequencies commonly ranging from 1 to 100 Hz to balance efficiency and avoid heating effects in the specimen.^[27] The stress ratio R = \frac{\sigma_{\min}}{\sigma_{\max}} characterizes the loading type, where R = -1 represents fully reversed tension-compression cycles, R = 0 indicates tension-tension loading with zero minimum stress, and other values like R = 0.1 simulate pulsating tension.^[26]^[28] Such protocols are foundational for establishing material fatigue properties, as they produce consistent data for S-N curve construction.^[29] Variable amplitude loading introduces fluctuations in stress or strain levels to better mimic non-uniform service environments, such as those in automotive or structural components. Block loading consists of sequential segments of constant amplitude cycles at different levels, allowing evaluation of cumulative damage across varying intensities.^[30] Random spectra, often modeled with a Gaussian distribution in aerospace applications, generate statistically representative irregular load histories derived from operational data.^[31] To analyze these complex signals, rainflow counting extracts equivalent constant amplitude cycles by identifying closed hysteresis loops, providing a standardized method for damage accumulation calculations under irregular loading.^[32]^[33] Spectrum loading sequences replicate entire service load histories in a condensed form, particularly for aerospace structures like aircraft wings, where standardized programs ensure comparability across tests. The FALSTAFF (Fighter Aircraft Loading STAndard For Fatigue purposes) sequence, developed from flight data of fighter aircraft, includes a mix of high- and low-amplitude cycles over 2 million events to simulate wing root stresses.^[34] Its miniaturized variant, Mini-FALSTAFF, condenses the spectrum to about 9,000 cycles while preserving key statistical features for efficient laboratory testing.^[35] These sequences incorporate overloads (peak high loads) and underloads (low or compressive loads), which influence crack propagation; overloads induce plastic zones that cause crack retardation by delaying growth, while underloads can accelerate it through closure effects.^[36]^[37] Environmental simulations integrate cyclic mechanical loading with external factors to assess synergistic degradation, such as in corrosive or thermally variable conditions. Combined mechanical-thermal cycling applies stress cycles alongside temperature fluctuations, replicating thermal fatigue in components like turbine blades where expansion-contraction exacerbates cracking.^[38] For corrosion fatigue, tests introduce aggressive media like saltwater solutions during loading to evaluate the combined effects of corrosion and cyclic stressing on material degradation.^[39] These protocols reveal how environmental interactions reduce fatigue life beyond mechanical loading alone.^[39]

Instrumentation and Execution

Measurement Techniques

Strain gauges are widely employed in fatigue testing to measure local strain on specimens, operating on the principle of resistance change in a conductive element under deformation. These devices typically utilize a Wheatstone bridge configuration, where four active or dummy gauges form a circuit that amplifies small resistance variations into measurable voltage outputs, enabling precise detection of tensile, compressive, or shear strains during cyclic loading.^[40]^[41] For multiaxial fatigue conditions, rosette patterns—arrangements of two or three gauges oriented at specific angles (e.g., 0°/45°/90° or 0°/60°/120°)—allow resolution of principal strains and stress states by combining measurements from multiple directions.^[42] Foil-type strain gauges, consisting of a thin metal foil grid bonded to a flexible backing, offer good conformity to curved surfaces and are suitable for moderate strain ranges up to about 5%, though they exhibit limited fatigue life under high-cycle conditions due to adhesive degradation.^[43] In contrast, semiconductor strain gauges, based on piezoresistive silicon elements, provide sensitivities 50-100 times higher than foil gauges, with superior fatigue endurance exceeding 10^7 cycles in dynamic applications, making them ideal for high-precision monitoring in advanced fatigue tests.^[44]^[41] Crack growth monitoring during fatigue testing relies on techniques that track crack initiation and propagation to quantify rates such as da/dN (crack length increment per cycle). Optical methods, including the traveling microscope, enable direct visual measurement of surface crack lengths with resolutions down to 0.01 mm by manually or mechanically traversing along the crack path under test illumination.^[45]^[46] The direct current potential drop (DCPD) technique measures crack extension indirectly by applying a constant current across the specimen and monitoring changes in electrical potential difference, which correlates linearly with crack length; calibration curves derived from compliance or optical data ensure accuracy for da/dN determination in metallic specimens under mode I loading.^[47]^[48] Acoustic emission (AE) detects crack initiation and early growth by capturing high-frequency elastic waves generated from microcrack formation or plastic deformation, with sensors placed near potential crack sites to record event counts, amplitudes, and rise times that signal damage accumulation before visible cracks form.^[49]^[50] Digital image correlation (DIC) has emerged as a non-contact method for full-field strain mapping in fatigue testing since the early 2000s, utilizing stereoscopic camera systems to track speckle patterns applied to the specimen surface. By comparing successive high-resolution images via cross-correlation algorithms, DIC computes in-plane and out-of-plane displacements with sub-pixel accuracy (typically 0.01-0.05 pixels), yielding 3D strain fields that reveal heterogeneous deformation zones and crack tip strain concentrations without physical sensors.^[51]^[52] This technique excels in capturing complex surface kinematics during cyclic loading, such as in biaxial fatigue setups, and integrates seamlessly with test execution for real-time validation of finite element models. Temperature monitoring is essential in fatigue testing to account for self-heating from plastic work, which can accelerate damage in high-strain regimes. Thermocouples, often ribbon-type (e.g., Type K or S) spot-welded or clamped to the specimen gauge length, provide point-wise measurements with response times under 1 second and accuracies of ±1°C, ensuring isothermal conditions or controlled thermal gradients as per standards like ISO 12106.^[53]^[54] Infrared thermography offers non-contact, full-field imaging of surface temperatures via thermal radiation detection, identifying localized hotspots (e.g., 5-20°C rises) indicative of dissipative plastic deformation during early fatigue stages, with spatial resolutions down to 0.1 mm using mid-wave or long-wave detectors.^[55]^[56]

Test Rigs and Setups

Fatigue test rigs encompass a range of mechanical systems designed to apply cyclic loads to specimens or structures, varying from small-scale laboratory setups to large full-scale configurations for simulating real-world conditions. These rigs ensure precise control over loading parameters to replicate fatigue mechanisms accurately.^[57] Small-scale rigs typically employ servo-hydraulic actuators for low- to mid-cycle fatigue testing, offering capacities up to 100 kN to accommodate standard material specimens. For instance, MTS Landmark systems utilize integrated actuator beams and hydraulic grips to deliver repeatable dynamic loads in tension, compression, or bending modes.^[57]^[58] Electromagnetic shakers, often electrodynamic in design, are preferred for high-frequency high-cycle fatigue (HCF) testing, enabling vibration frequencies up to several kilohertz to accelerate tests on small components like turbine blades.^[59]^[60] Full-scale setups involve multi-actuator frames to impose complex, multi-axial loads on large structures, such as aircraft wings, using 4-6 hydraulic jacks to mimic operational stresses. These configurations, as seen in wing fatigue rigs, apply distributed forces across the structure to evaluate overall durability.^[61]^[62] Resonance testing enhances efficiency in HCF for full-scale applications by exciting the specimen near its natural frequency, reducing energy input while achieving millions of cycles rapidly.^[63]^[64] Control systems in these rigs rely on closed-loop feedback mechanisms to maintain precise load or displacement profiles, incorporating load cells for force measurement and extensometers for strain monitoring. Software platforms like LabVIEW facilitate waveform generation and real-time adjustments, ensuring synchronization with test protocols across various specimen geometries.^[65]^[66]^[67] Safety features are integral to prevent equipment damage or hazards, including overtravel limits on actuators to restrict excessive motion and emergency stop buttons for immediate halt. Adaptations for environmental chambers allow integration with vacuum systems for altitude simulation or humidity controls to assess corrosion-fatigue interactions, maintaining test integrity under non-ambient conditions.^[68]^[69]^[70]

Analysis and Interpretation

Data Processing Methods

Data processing in fatigue testing involves extracting key parameters such as cycle counts, stress-life relationships, and cumulative damage from raw signals like load, stress, or strain histories. These methods ensure accurate fatigue life predictions by handling variability in loading and noise in measurements. Raw data from tests, often acquired at high sampling rates, require preprocessing to remove artifacts before applying specialized algorithms. Cycle counting identifies individual fatigue cycles from irregular loading histories, essential for variable amplitude tests. The rainflow method, standardized in ASTM E1049-85(2023), simulates rain flowing down a pagoda roof to extract closed hysteresis loops, counting cycles based on stress range and mean, which correlates well with damage.^[71] For low-cycle fatigue (LCF), where plastic deformation dominates, hysteresis loop analysis quantifies plastic strain amplitude from stabilized loops. This enables application of the Coffin-Manson relation, \Delta \epsilon_p / 2 = \epsilon_f' (2N_f)^c, linking plastic strain range to cycles to failure N_f, with \epsilon_f' as fatigue ductility coefficient and c as fatigue ductility exponent. Curve fitting constructs empirical models from test data to represent fatigue behavior. Least-squares regression on log-log plots fits S-N curves, minimizing residuals between observed stress amplitudes and logarithmic fatigue lives across multiple specimens.^[72] For runout tests, where specimens survive beyond a threshold cycles without failure, probabilistic modeling assumes log-normal distributions for life scatter, estimating survival probabilities and curve scatter parameters via maximum likelihood. Damage accumulation quantifies total degradation under multiaxial or block loading. Miner's linear rule sums fractional damages, D = \sum (n_i / N_i) = 1 at failure, where n_i is applied cycles at stress level i and N_i is cycles to failure from the S-N curve; however, it overpredicts life under high-low sequences due to load interaction effects. Nonlinear alternatives, such as the Marco-Starkey model, introduce damage curve functions f(S_i) to weight contributions by stress severity, addressing sequence sensitivity: D = \sum [n_i f(S_i) / N_i] = 1. Software tools facilitate automated post-processing of fatigue data. MATLAB implements rainflow counting per ASTM E1049-85(2023) and supports Miner's rule integration for damage spectra.^[73] Commercial packages like FE-safe perform advanced cycle extraction, curve fitting, and probabilistic assessments from finite element outputs.^[74] Recent advances incorporate machine learning (ML) techniques, such as neural networks and random forests, for enhanced prediction of fatigue life from complex datasets, improving accuracy in variable amplitude and multiaxial loading scenarios as demonstrated in studies up to 2025.^[75]^[76] Noise filtering, typically via low-pass Butterworth filters, preprocesses strain signals to attenuate high-frequency artifacts while preserving cycle amplitudes below 10-20 Hz for most metallic tests.^[77] Processed data then informs S-N curve construction for life estimation.

Failure Assessment

Failure assessment in fatigue testing involves detailed post-test examinations to evaluate the mechanisms and extent of crack initiation, propagation, and final fracture, ensuring that observed outcomes align with predictive models for material reliability. Post-test inspections typically include fractographic analysis using scanning electron microscopy (SEM) to identify and count fatigue striations on fracture surfaces, which provide a direct measure of crack growth rate approximated as da/dN per cycle.^[78]^[79] These striations, formed during cyclic loading, allow estimation of the number of cycles endured before failure by correlating striation spacing with propagation rates.^[80] Additionally, non-destructive techniques such as dye penetrant testing reveal surface crack lengths by highlighting discontinuities, while ultrasonic methods detect and measure internal crack dimensions through reflection or transmission signals.^[81]^[82] Common failure indicators observed in these inspections include beach marks—conchoidal patterns on fracture surfaces representing discrete stages of crack advancement due to load variations—and distinctions between transgranular fracture paths, which exhibit cleavage-like features across grains, and intergranular paths, characterized by decohesion along grain boundaries resembling a "rock candy" appearance.^[83]^[84] These features help differentiate fatigue-dominated failure from overload or environmental influences. For crack propagation assessment, striation data can be briefly referenced to empirical relations like Paris' law, which models da/dN as a function of stress intensity factor range.^[85] Life comparison evaluates the predicted fatigue life (N_f) against observed cycles to failure, accounting for inherent variability through scatter bands typically spanning ±3 standard deviations to encompass 99.7% of data distribution.^[22] Runout criteria define non-failure as survival beyond 10^7 cycles, indicating an endurance limit where no further degradation occurs under the applied loading. Validation metrics further assess reliability by applying factors of safety, such as 3-4 for aircraft components, to ensure predicted lives exceed operational demands while correlating experimental results with finite element simulations for stress-strain accuracy.^[86]^[87] This correlation confirms model fidelity, with discrepancies often refined iteratively to match observed fracture patterns and life data.^[88]

Applications and Standards

Industrial Uses

Fatigue testing plays a critical role in the aerospace industry, where components such as aircraft wings and fuselages must endure millions of load cycles to ensure airworthiness and prevent catastrophic failures during service. Full-scale fatigue programs simulate operational conditions, including pressure cabin cycles, wing bending, and landing impacts, to assess structural integrity over the aircraft's design life. For instance, the Boeing 787 Dreamliner's full-scale fatigue test subjected the airframe to over 160,000 simulated flights, equivalent to more than three times the expected service life of 44,000 cycles, confirming the durability of its predominantly composite primary structure without significant cracking.^[89]^[90] In the automotive sector, fatigue testing evaluates the longevity of chassis components and engine parts under repeated loading from road vibrations, impacts, and thermal cycling to guarantee vehicle reliability over extended mileage. Suspension systems, in particular, are subjected to cyclic loading that mimics rough road conditions, often accelerated to represent high-mileage usage. Typical tests for suspension elements apply multi-axial loads to identify crack initiation and propagation in materials like steel and aluminum alloys.^[91] Civil engineering applications of fatigue testing focus on infrastructure elements like bridge girders, which experience variable amplitude loading from traffic volumes and weights, to predict service life and inform maintenance schedules. Load spectra derived from weigh-in-motion data replicate real-world truck passages, applying cyclic stresses to girder sections to evaluate weld fatigue and distortion-induced cracking. For wind turbine blades, testing incorporates gust loading profiles to simulate turbulent wind conditions, using resonant excitation methods to accelerate damage accumulation in composite materials and assess delamination risks under flapwise bending.^[92]^[93] Biomedical engineering employs fatigue testing for orthopedic implants, such as hip prostheses, to verify performance under physiological loading that mimics daily activities like walking. According to ISO 7206-4, stems and necks are cyclically loaded in a simulated body environment to 5 million cycles, representing approximately 5 years of use at 1-2 million steps per year, ensuring no fracture or excessive deformation occurs.^[94]^[95] In the energy sector, fatigue testing of pipelines assesses resistance to cyclic pressure fluctuations and external loads in corrosive media like sour gas or seawater, where environmental factors accelerate crack growth. Tests immerse steel samples in H2S or CO2 solutions while applying alternating stresses to quantify corrosion-fatigue life reduction. For gas turbine blades, evaluation combines high-cycle fatigue with hot corrosion exposure, simulating operational environments with salt ingestion and thermal gradients to prevent intergranular cracking in nickel-based superalloys.^[96]^[97]^[98]

Regulatory Standards

Fatigue testing in engineering and materials science is governed by a range of international and national standards that ensure consistency, reliability, and safety in evaluating material endurance under cyclic loading. These standards specify procedures for test execution, data analysis, and interpretation to support design validation across industries. Key organizations such as the American Society for Testing and Materials (ASTM) and the International Organization for Standardization (ISO) provide foundational guidelines, while sector-specific regulatory bodies enforce certification requirements. In the United States, ASTM International develops widely adopted standards for fatigue testing of metallic and composite materials. ASTM E466 outlines the procedure for conducting force-controlled constant amplitude axial fatigue tests on metallic materials to determine fatigue strength in the elastic strain regime, emphasizing specimen preparation, loading parameters, and runout criteria.^[99] Complementing this, ASTM E647 provides a test method for measuring fatigue crack growth rates (da/dN) in metallic materials, covering near-threshold to instability regimes using compact tension or middle-crack tension specimens under constant amplitude loading. For statistical evaluation, ASTM E739 guides the analysis of linear or linearized stress-life (S-N) and strain-life (ε-N) fatigue data, incorporating methods to estimate mean and standard deviation for reliability assessments, including scatter factors for design curves.^[100] International equivalents under ISO harmonize with ASTM practices while addressing global needs. ISO 12106 specifies the axial-strain-controlled method for fatigue testing of metallic materials, detailing uniaxial specimen deformation at constant amplitude, uniform temperature, and strain ratio R = -1, suitable for low-cycle fatigue evaluation. For composites, ISO 13003 defines procedures for determining fatigue properties of fibre-reinforced plastics under cyclic loading at constant amplitude and frequency, including tension-tension, compression-compression, and reversed loading modes, with guidance on specimen geometry and environmental controls.^[101] Certification processes integrate these standards into regulatory frameworks for high-stakes applications. In aviation, the Federal Aviation Administration (FAA) under 14 CFR Part 25 requires damage-tolerance and fatigue evaluation of metallic structures, where safe-life designs must demonstrate endurance for the prescribed service life without detectable cracks, supported by analysis, full-scale testing, or a combination, often incorporating scatter factors for variability. The Joint Aviation Requirements (JAR), harmonized with FAA, similarly mandate fatigue substantiation, typically requiring demonstration of at least the design service life with safety margins to prevent widespread fatigue damage. For oil and gas components, the American Petroleum Institute (API) standard 17TR8 provides guidelines for high-pressure high-temperature (HPHT) subsea equipment, including fatigue screening and life-cycle estimation using stress-life or fracture mechanics approaches, with validation testing to confirm design lives under cyclic wave and operational loads. Recent updates in the 2020s reflect evolving technologies and methodologies. ASTM E466 was revised in 2021 to incorporate improved alignment verification and data reporting for enhanced reproducibility.^[99] Similarly, ASTM E647 saw a 2024 update emphasizing near-threshold data for steady-state crack growth rates. These revisions increasingly integrate probabilistic methods, as in ASTM E739's statistical frameworks for S-N curve reliability, to account for material variability and support risk-based designs. For additive manufacturing, emerging guidelines within ASTM Committee F42 address fatigue of as-built parts, adapting traditional tests like E466 to account for anisotropy, surface roughness, and defects, with ISO/ASTM 52909 providing supplementary evaluation for metal AM mechanical properties including fatigue. Such updates ensure standards accommodate probabilistic fatigue life predictions and AM-specific effects like porosity on crack initiation. Compliance with these standards involves third-party validation to verify test integrity and results applicability. Accredited laboratories, such as those certified under ISO/IEC 17025, conduct independent audits of test setups, instrumentation calibration, and data acquisition to confirm adherence. Documentation of test matrices—detailing specimen details, loading histories, environmental conditions, and failure modes—is mandatory for certification submissions, enabling traceability and reproducibility in regulatory reviews.

Notable Fatigue Tests

Historical Case Studies

One of the earliest and most influential cases in fatigue testing history occurred with the de Havilland Comet, the world's first commercial jet airliner, which suffered two catastrophic in-flight disintegrations in 1954. The initial accident involved BOAC Flight 781 on January 10, crashing into the Mediterranean Sea near Elba, Italy, followed by South African Airways Flight 201A on April 8 near Naples, Italy, both attributed to metal fatigue in the pressure fuselage. Extensive post-accident investigations, including full-scale fatigue testing of a Comet airframe at the Royal Aircraft Establishment in Farnborough, revealed that square-shaped windows and cutouts created severe stress concentrations at their corners, accelerating crack propagation under repeated pressurization cycles. These tests, simulating thousands of flight hours, demonstrated that the aluminum alloy fuselage failed at stresses far below initial design limits due to undetected fatigue cracks initiating from these geometric flaws. As a direct result, subsequent Comet redesigns incorporated rounded windows and reinforced structures, fundamentally altering aircraft design practices to prioritize fatigue-resistant geometries.^[102]^[103]^[104] During World War II, the mass-produced Liberty ships exemplified failures related to weld imperfections, with over 2,700 vessels built using inexperienced welders and unproven welding techniques. Starting in 1943, incidents like the SS Schenectady fracturing in half while docked in Portland, Oregon, on January 16, highlighted brittle fractures propagating from weld defects such as inclusions and lack of fusion, often under low-temperature conditions that reduced steel ductility. Post-failure investigations and fracture tests on Liberty ship hull sections, conducted by the U.S. Navy and metallurgists, confirmed that these weld defects acted as crack initiators. While some at-sea failures involved cyclic loading from ocean waves contributing to crack growth, the primary mechanism was brittle fracture. These investigations, involving scaled models and full-scale weld inspections, spurred the development of fracture mechanics principles, including the concept of fracture toughness, and led to improved welding standards like preheating and post-weld heat treatment to mitigate such risks.^[105]^[106]^[107] The 1988 incident involving Aloha Airlines Flight 243, a Boeing 737-200, provided critical insights into fatigue in aging aircraft structures during high-cycle operations. On April 28, the aircraft experienced an explosive decompression at 24,000 feet near Maui, Hawaii, when an 18-foot section of the upper fuselage tore away, yet the pilots safely landed with 94 passengers and crew aboard. NTSB-led fatigue testing of recovered fuselage panels and simulated lap joints revealed that multiple fatigue cracks had originated from countersunk rivet holes in the overlapping fuselage splices, propagating undetected due to disbonding of sealant and cold-bonding adhesives. Full-scale tests on similar Boeing 737 lap joint specimens, pressurized to mimic approximately 90,000 flight cycles, showed that corrosion pits in the aluminum exacerbated crack initiation and growth, while multi-site damage—simultaneous cracking at numerous rivet lines—reduced residual strength and prevented load redistribution. This case prompted the FAA to mandate enhanced inspections for aging high-time aircraft, influencing damage tolerance certification rules.^[108]^[109]^[110] Historical fatigue tests from these cases underscored the pivotal role of corrosion in accelerating crack propagation, as seen in the marine exposure of Liberty ships and the salt-laden environment affecting Aloha's fuselage, where galvanic corrosion between aluminum and fasteners created initiation sites. Similarly, multi-site damage emerged as a key factor, particularly in the Comet's window clusters and Aloha's riveted lap joints, where linked cracks overwhelmed structural redundancy under cyclic loads. These findings have informed modern standards by emphasizing environmental factors and probabilistic damage assessments in fatigue life predictions.^[111]^[112]^[113]

Modern Examples

In the 2020s, fatigue testing of additively manufactured (AM) parts has highlighted the challenges of anisotropy in materials like Ti-6Al-4V, particularly in lattice structures used for aerospace applications. A 2023 study on laser additively manufactured (LAM) Ti-6Al-4V alloy demonstrated obvious anisotropic fatigue properties, with fatigue strength varying significantly based on build orientation; parallelly deposited specimens exhibited higher fatigue limits (approximately 470 MPa) compared to transversely deposited ones (around 430 MPa) due to differences in microstructure and defect distribution along the build direction.^[114] Similarly, fatigue tests on diamond-based Ti-6Al-4V lattice structures produced by laser powder bed fusion (L-PBF) in 2022 revealed that load direction relative to the build orientation strongly influences endurance, with as-built lattices showing reduced fatigue resistance owing to surface roughness and internal pores aligned anisotropically.^[115] These findings underscore the need for orientation-optimized designs in AM components to mitigate direction-dependent crack initiation and propagation. Full-scale fatigue testing of composite materials in wind turbine blades has advanced to accommodate larger scales and harsher environmental simulations. In 2023, researchers conducted full-scale validation tests on a composite wind turbine blade using an inertia generator system to replicate cyclic loading; the blade underwent 1 million flapwise and 2 million edgewise cycles at a load ratio of R = -1, with bending moments verified through finite element analysis and strain measurements. This approach, simulating real-world gust-induced bending moments on blades approaching 100 meters in length, confirmed the efficacy of carbon fiber-reinforced polymer (CFRP) layups in distributing fatigue damage. Such tests at facilities like those operated by the National Renewable Energy Laboratory (NREL) emphasize the role of resonance excitation in accelerating validation while maintaining spectral loading fidelity to offshore conditions.^[116] Fatigue testing for electric vehicle (EV) batteries has evolved to assess structural integration under cyclic mechanical loads, combining vibration and impact simulations. A 2024 review of lithium-ion battery packs in EVs highlighted cyclic loading tests for structurally integrated designs, where battery enclosures serve as chassis elements; standards such as IEC 62660-2 (10–2000 Hz vibrations) and SAE J2380 (simulating 100,000 miles) are used to evaluate degradation under road-like conditions. Hybrid crash-fatigue protocols, incorporating low-velocity impacts followed by endurance cycling, are critical for vehicles where the pack contributes to overall rigidity.^[117] Innovations in fatigue testing incorporate artificial intelligence (AI) for real-time prediction, enhancing ongoing assessments in aviation. In the EU-funded Clean Sky 2 program, concluded in 2024, structural health monitoring (SHM) systems were validated for real-time tracking in composite structures, improving safety and reducing maintenance costs through sensor integration. As of 2025, the successor Clean Aviation Joint Undertaking continues these efforts, focusing on advanced SHM technologies for sustainable aircraft designs aligning with standards like EASA CS-25.^[118]^[119]^[120]

References

[1]
What is Fatigue Testing?
Fatigue testing is defined as the process of progressive localized permanent structural change occurring in a material subjected to conditions that produce ...
[2]
Fatigue Testing - an overview | ScienceDirect Topics
Fatigue testing is defined as an assessment method used to evaluate the durability and fatigue life of materials by subjecting them to cyclic loading to ...<|control11|><|separator|>
[3]
[PDF] 1 CHAPTER 12 FATIGUE 12.1 Fatigue Failure of Materials 12.2 ...
Fatigue failure of materials refers to their failure under the action of cyclic elastic stress. Fatigue generally involves the formation and gradual growth of ...
[4]
Introduction to the ASTM E606 Standard - Laboratory Testing Inc.
Oct 23, 2024 · ASTM E606 is a comprehensive standard used to evaluate the fatigue behavior of metallic materials.
[5]
Fatigue of Metals: Part One - Total Materia
Fatigue failure is defined as a material's tendency to fracture through progressive brittle cracking under repeated alternating or cyclic stresses considerably ...
[6]
[PDF] Mechanisms of Fatigue Crack Initiation and Growth
Fatigue crack mechanisms include initiation and growth, with stages I and II. Initiation involves cell structure development and PSB formation. The cyclic ...
[7]
Fatigue Properties: Part One - Total Materia
Fatigue failure occurs through a well-defined three-stage process: crack initiation, slow stable crack growth, and rapid fracture. Understanding each stage ...
[8]
[PDF] Fatigue | MIT
May 1, 2001 · A more general sort of fatigue testing adds a mean stress σm on which a sinusoidal cycle is superimposed, as shown in Fig. 6. Such a cycle can ...
[9]
corrosion fatigue | Total Materia
Corrosion fatigue occurs through accumulated load cycling resulting in localized irreversible cyclic plastic deformation with as a result of chemical or ...
[10]
Microstructural mechanisms of cyclic deformation, fatigue crack ...
Mar 28, 2015 · In addition, intercrystalline fatigue damage can occur at grain boundaries. In heterogeneous materials containing inclusions or pores, these ...
[11]
Fatigue crack nucleation at interfaces - ScienceDirect.com
Fatigue crack nucleation depends on the local microstructure of the material, the internal stress distribution and the external loading conditions. Cracks ...
[12]
Effects of inclusions, grain boundaries and grain orientations on the ...
The results show that, potential fatigue cracks tend to nucleate along coarse and closely spaced inclusion particles or high-angle GBs.Missing: nucleation | Show results with:nucleation
[13]
[PDF] fundamentals - of metal fatigue analysis
The basis of the stress-life method is the Wöhler or S-N diagram, which is a plot of alternating stress, S, versus cycles to failure, N. The most common ...
[14]
High-Cycle, Low-Cycle, Extremely Low-Cycle Fatigue and ... - NIH
... HCF resistance requires a high monotonic tensile strength [35], where the stress-based Basquin law is often used to estimate the HCF life. In contrast, LCF ...
[15]
[PDF] An Investigation on the Semi-Empirical and Computational High ...
Jun 25, 2024 · The need for High Cycle Fatigue (HCF) analysis and its distinction from other fatigue methods ... Basquin's Law of Fatigue,". Phys. Rev. Lett., ...
[16]
O. H. Basquin, “The Exponential Law of Endurance Tests,” American ...
O. H. Basquin, “The Exponential Law of Endurance Tests,” American Society for Testing and Materials Proceedings, Vol. 10, 1910, pp. 625-630.Missing: original | Show results with:original
[17]
[PDF] Fatigue
For ferrous metals, S-N plots are characterized by a knee. The "knee of the plot " generally occurs around. 1 000 000 cycles and is called the endurance limit.
[18]
Fatigue Endurance Limit of Steel - Scholars' Mine
Jan 1, 2001 · A simple rule of thumb calculation for the fatigue limit is one-half of the ultimate tensile strength.
[19]
[PDF] evaluation of the effect of surface finish on high-cycle fatigue of slm ...
Typically, the “as-built” (AB) surfaces are much rougher than machined surfaces, and that surface roughness can affect the fatigue life of a part. Generally ...
[20]
[PDF] Influence of Testing and Material Factors on the Fatigue Strength of ...
Here, the fatigue limit is defined as the stress at which 50 per cent of the test specimens can stand up to 2 x 1.06 load cycles. l"eliable. As a l"ule, ...<|control11|><|separator|>
[21]
[PDF] Statistical Summaries of Fatigue Data for Design Purposes
S-N fatigue data implicitly assume that cycles to failure has a lognormal distribution. The three-parameter. Weibull (TPW) is often proposed in the fatigue.
[22]
A modification in Weibull parameters to achieve a more accurate ...
Among the probability distributions used to analyze fatigue problems, the Weibull distribution is one of the most common models in the logarithmical scale.
[23]
Standard Test Method for Measurement of Fatigue Crack Growth ...
Mar 16, 2023 · 1.4 A range of specimen sizes with proportional planar dimensions is provided, but size is variable to be adjusted for yield strength and ...
[24]
Stress gradient as a size effect in fatigue life determination for ...
The stress gradient in bending acts as a size effect, increasing fatigue life, similar to small specimens, and is a type of geometric size effect.
[25]
Stress-Life Fatigue Testing Basics | 2017-08-01 | Quality Magazine
Aug 1, 2017 · Stress Ratio, R – equals -1 for fully reversed loading. R = Smin/Smax. Amplitude Ratio, A – infinite for fully reversed loading. A = Sa/Sm ...
[26]
Fatigue life: Definition and description | ZwickRoell
A fatigue life test with constant amplitudes is referred to as S-N test, where the tolerable stress amplitude is determined using the corresponding number of ...Missing: sinusoidal waveform frequency
[27]
[PDF] Cyclic Fatigue Testing of Adhesive Joints Test Method Assessment
Constant amplitude (sinusoidal waveform) fatigue tests were carried out on all three test configurations in load control with the stress ratio R (σMIN/σMAX) ...
[28]
[PDF] FATIGUE TESTS AND STRESS-LIFE (S-N) APPROACH - EFatigue
For axial loaded unnotched specimens, a nominal stress gradient does not exist, and the average and maximum nominal stresses have the same magnitude resulting ...
[29]
Fatigue testing under variable amplitude loading - ScienceDirect.com
This paper aims at presenting how spectra and test conditions should be clearly described and how statistics can be applied when variable amplitude test ...
[30]
[PDF] RANDOM LOADING FATIGUE CRACK GROWTH - 19
Aug 14, 1987 · The normal (or Gaussian) distribution is commonly applied to random pro- cesses of engineering interest. It has two parameters, the mean, p ...
[31]
[PDF] FATIGUE FROM VARIABLE AMPLITUDE LOADING - EFatigue
An advantage of rainflow counting is when it is used with notch strain analysis. ▫ Note that the rainflow counting results in closed hysteresis loops, with each.
[32]
[PDF] cycle counting for variable amplitude crack growthi
It is now well estab- lished that rainflow counting gives the best life estimates for strain cycle fatigue tests under variable amplitude loading (6-7).
[33]
[PDF] FATIGUE CRACK GROWTH PREDICTION UNDER FALSTAFF ...
The original FALSTAFF load sequence [11] is shown in Figure 1. This spectrum was produced from actual flight records of the wing-root loads from four different ...
[34]
Fatigue life of a carbon fiber composite T-joint under a standard ...
Sep 1, 2015 · The fatigue life of composite T-joint predicted under mini-FALSTAFF load sequence compare quite well with experimental results. •. The accuracy ...
[35]
[PDF] Analysis of aircraft load spectrum by means of flight simulator
Figure 41: Crack growth retardation due to overload. Now that the importance of retardation phenomena in the crack growth under VA loading has been ...
[36]
[PDF] The Merging of Fatigue and Fracture Mechanics Concepts
At present, fatigue is characterized by a crack initiation stage (NO and a crack-propagation stage (Np); and crack propagation is characterized by the ...
[37]
[PDF] High-Temperature Fatigue Behaviour of Austenitic Stainless Steel
Dec 14, 2018 · The aim of this licentiate thesis is to increase the knowledge of the me- chanical behaviour at high temperature cyclic conditions for ...
[38]
[PDF] IMPROVING CORROSION FATIGUE PERFORMANCE & DAMAGE ...
All testing was performed in a neutral solution of 3.5% weight sodium chloride and distilled water according to the guidelines of ASTM G5-94. A saturated ...
[39]
[PDF] Enhanced Fatigue Crack Propagation in Structural Alloys for ...
The approach couples empirical modeling of environmental. FCP rates with corrosion fatigue experiments. Three different computer models have been developed and ...
[40]
Principles, Types and Configurations of Strain Gauges - IQS Directory
The Wheatstone bridge circuit amplifies minute resistance changes in strain gauges, providing high-resolution voltage outputs crucial for accurate force, ...
[41]
Understanding Strain Gauges in Load Cells (Thin Film vs. Bonded ...
Jul 30, 2019 · Typically, four strain gauges are used in a Wheatstone Bridge configuration to make up a load cell (a.k.a force sensor).
[42]
One to Five | The Essential Blog for Engineers | StrainBlog
Jun 30, 2021 · A strain gage rosette is, by definition, an arrangement of two or more closely positioned gage grids, separately oriented to measure the normal ...
[43]
Strain Gages - FAQ | KYOWA
A foil strain gage consists of a metal foil sandwiched between resin films. When metal materials are elongated or contracted, their electrical resistance ...
[44]
Semiconductor vs Foil Strain Gauge Load Cells, Which Is Better?
Fatigue Life. Silicon-type semiconductor strain gauges have an extremely long fatigue life as compared to foil gauges. This is an important issue for tension ...
[45]
Methods for automated crack length detection in fracture mechanical ...
For polymers, it is still state of the art to measure the crack length manually by the use of a travelling microscope. ... Standard Test Method for Measurement of ...
[46]
Traveling microscope to measure the steel-plate crack propagation.
To measure the crack length, a traveling microscope (manufactured by Spindler & Hoyer, Germany) with a resolution of 0.01 mm was installed on the lower grip of ...
[47]
Numerical calibration and experimental validation of the direct ...
The Direct Current Potential Drop (DCPD) method has been investigated to estimate the crack size in axial fatigue tests of single-edge-crack round bars.Missing: optical traveling
[48]
[PDF] Recording of Elevated Temperature Fatigue Crack Growth Data by ...
May 6, 2011 · The DCPD method, used in this investigation, was found to record and correlate the potential difference in terms of crack growth rate (da/dN) ...
[49]
Experimental Investigation of Fatigue Crack Growth Behavior ... - NIH
Mar 1, 2021 · The fatigue tests were performed on an Instron testing machine and the crack growth rates were measured. Moreover, the acoustic emission ...
[50]
Acoustic Emission Monitoring of Fatigue Crack Growth in Hadfield ...
Jul 20, 2023 · This paper focuses on the study of acoustic emission (AE) behaviour and its correlation with fatigue crack growth in Hadfield steel during bending fatigue ...
[51]
The application of digital image correlation (DIC) in fatigue ...
Dec 29, 2022 · DIC is a noncontact method that uses a series of digital images to calculate full-field strains on the surface of an object, planer or curved.
[52]
Digital image correlation for continuous mapping of fatigue crack ...
The full-field digital image correlation (DIC) technique was used to identify crack initiation and early crack growth on irregular, corroded surfaces from ...
[53]
[PDF] Product Information Thermomechanical Fatigue Testing System
temperature control with ribbon thermocouples. • Temperature measurement is carried out with standard-compliant ribbon thermocouples in the center of the ...
[54]
https://www.iso.org/obp/ui/en/#!iso:std:79650:en
[55]
Infrared Thermography for Temperature Measurement and Non ...
This paper presents a review of infrared thermography especially focused on two applications: temperature measurement and non-destructive testing.
[56]
Thermography: A New Nondestructive Evaluation Method in Fatigue ...
Thermography can potentially provide an effective method to in-situ monitor temperature evolution and material stress-strain behavior during fatigue.
[57]
Landmark Servohydraulic Test Systems - MTS Systems
From complex thermomechanical fatigue studies to standard tension and compression tests, MTS Landmark systems deliver accurate, repeatable results.
[58]
[PDF] MTS Landmark® Testing Solutions
MTS Landmark systems are ideal for the exacting demands of material fatigue testing. Highly stiff integrated actuator beams, patented hydraulic grips, high ...Missing: rigs | Show results with:rigs
[59]
An Ultra-High Frequency Vibration-Based Fatigue Test and Its ...
This paper proposes an ultra-high frequency (UHF) fatigue test of a titanium alloy TA11 based on electrodynamic shaker in order to develop a feasible testing ...
[60]
High-Force LDS Shakers - HBK
A water-cooled electrodynamic shaker for shock and high-performance vibration testing of large devices, such as aircraft components up to 907 kg (2000 lb).
[61]
[PDF] A Record of the Australian Mirage Wing Fatigue Test
A full-scale fatigue test was completed in August 1974 on a Mirage III0 starboard wing utilising a loading spectrum as specified by the Royal Australian Air ...Missing: setups | Show results with:setups
[62]
[PDF] Static and Fatigue Testing of Full-Scale Aircraft Structures
These test programs use state-of-the-art equipment to provide hydraulic load and fuselage pressurization con- trol combined with data acquisition hardware for ...Missing: multi- actuator jacks
[63]
Full-Scale Fatigue Testing using the Resonance Method - TWI Global
Resonance fatigue testing involves exciting a test specimen close to its first mode of vibration by applying a rotating radial force to one end.
[64]
Dynamic Materials Testing: Which Drive is Right for My Requirements?
Aug 11, 2025 · Resonance systems: energy efficiency meets high frequency. When it comes to fatigue resistance and high-cycle fatigue (HCF), resonance testing ...
[65]
An experimental and numerical investigation into tensile fatigue ...
In combination with an FPGA card, an NI/LabVIEW® programme was built to control the loading machine, record the tensile strain data from the extensometer and ...
[66]
Mechanical and Environmental Testing Laboratory (METLab)
Two Instron/MTS closed-loop servohydraulic testing systems with the Instron WaveMatrixTM software package for performing low-cycle fatigue, creep-fatigue, crack ...
[67]
[PDF] Fatigue Analysis in LabVIEW - ni
LabVIEW Fatigue Analysis consists of a set of VIs for stress-life based fatigue analysis. Analysis functions include peak and trough detection, rainflow cycle ...Missing: control systems closed- feedback cells extensometers
[68]
Expert Answers to Common Environmental Test Chamber Questions
Nov 13, 2024 · AES SAFE chambers come with another level of protection and safety features like emergency stops, temperature limits, and more. Any chamber can ...Missing: fatigue vacuum
[69]
HAST - Highly Accelerated Stress Test Chambers
Safety Features: Overheat & over-pressure protectors; Door lock safety mechanism to prevent opening of the door while the chamber is pressurized; Specimen ...Missing: fatigue vacuum
[70]
Altitude Chambers with Temperature and Humidity Controls from CSZ
CSZ Altitude test chambers offer the option of not only testing products for temperature and humidity, but also variations in air pressure.Missing: fatigue overtravel stops
[71]
Standard Practices for Cycle Counting in Fatigue Analysis - ASTM
Dec 6, 2023 · These practices cover the procedures used to obtain cycle counts by various methods, including level-crossing counting, peak counting, simple-range counting, ...
[72]
[PDF] best-practice-guide-on-statistical-analysis-of-fatigue ... - TWI Global
data, the maximum likelihood method leads to the least squares function on which linear regression is generally based.19 In the general case, numerical ...
[73]
Rainflow counts for fatigue analysis - MATLAB - MathWorks
c = rainflow(x) returns cycle counts for the load time history, x, according to the ASTM E 1049 standard. See Algorithms for more information.
[74]
https://www.3ds.com/products/simulia/fe-safe/
[75]
[PDF] Using Basic Signal Filters - Epsilon Technology
Low-pass filters improve signal quality by filtering noise, especially when the noise is higher frequency. Filters can be in instruments, software, or post- ...
[76]
Fractographic Analysis of Fatigue Striations Formation ... - NASA ADS
Counting and measuring fatigue striations is a method in estimating the number of loading cycles a component went through until fracture. Some studies suggest a ...
[77]
Methods for evaluating fracture patterns of polycrystalline materials ...
At present, fractographic analysis of fatigue fracture is based on measuring the parameters of fatigue striations and evaluating the parameters of dimple relief ...
[78]
[PDF] On Fatigue Striations - Scientia Iranica
Fatigue striations are a characteristic of fatigue crack growth, observed by light microscopy, and are a saw-tooth pattern. Counting them can reveal prior ...
[79]
[PDF] Dye penetrant crack detectability in external corners in presence of ...
NASA uses special dye penetrant nondestructive evaluation process to provide reliable detection of very small cracks. Typically the surface crack lengths ...
[80]
[PDF] Ultrasonic technique for detection and measurement of fatigue cracks
An ultrasonic system uses reflection to detect minute fatigue cracks, and through-transmission for longer cracks. It is more easily applied than other methods.
[81]
[PDF] A BRIEF HISTORY OF FRACTOGRAPHY
Macroscopically visible 'conchoidal' markings (also called 'beach markings' etc.) on fatigue fracture surfaces would probably have been observed for failures of ...
[82]
[PDF] FRACTOGRAPHY OF METALS AND PLASTICS
Cleavage is characteristic of transgranular brittle fracture. Intergranular fracture, recognizable by its “rock candy” appearance, occurs when the crack path ...
[83]
[PDF] fatigue crack propagation
The power law form of fatigue crack growth law was first proposed by Paris, Gomez, and Anderson, and is often referred to as the “Paris law.” 10. Page 11. , ...
[84]
[PDF] AC 23-13A - Fatigue, Fail-Safe, and Damage Tolerance Evaluation ...
Sep 29, 2005 · The goal of the fatigue requirements is to maintain the design strength capability, both limit and ultimate load, throughout the operational ...
[85]
A finite element simulation and experimental validation of a ...
The paper describes the FE modelling and experimental validation of a composite bolted joint loaded in bending and torsion. The selected material is a ...
[86]
Correlation between predicted fatigue life and experimental test ...
The procedure involves estimating stress intensity factors (SIFs), crack trajectory, and fatigue life, using two different softwares in both two and three- ...
[87]
Dreamliners don't crack: Boeing 787 survives extensive fatigue testing
Dec 3, 2015 · A five-year fatigue test simulated more than 160,000 take-offs and landings, more than the design life of 44,000 cycles, says a report in ...
[88]
Dreamliners don't crack: Boeing 787 survives fatigue testing
Dec 2, 2015 · That's the result of a five-year fatigue test of the third 787 built, which has been through a mechanized stress test mimicking more than 160, ...
[89]
Durability Testing - Automotive Testing and Development Services
ATDS is ready to conduct your mileage accumulation test program whether for ten or ten million miles. As a full service independent automotive testing firm ...
[90]
Ford burns through 1 million miles on EcoBoost test engines
Sep 3, 2008 · Word comes from Ford today that they've racked up over one million miles on their EcoBoost test engines in combined real-world driving and in-lab testing.Missing: automotive | Show results with:automotive
[91]
[PDF] Design and Evaluation of Steel Bridges for Fatigue and Fracture
This Manual covers a full range of topics related to fatigue and fracture in steel bridges, including analysis, design, evaluation, repair, and retrofit.
[92]
Fatigue testing and analysis of I-girders with trapezoidal corrugated ...
Oct 1, 2019 · However, girders with trapezoidal corrugated webs are susceptible to fatigue under inevitable repeated heavy traffic loads ...
[93]
ISO 7206-4, 7206-6 and 7206-8 - Instron
A guide to cyclic fatigue testing of artificial hip implant prostheses in accordance with ISO 7206-4, ISO 7206-6, ISO-7206-8 and ASTM F2068.
[94]
[PDF] Hip stem fatigue: : The implications of increasing patient mass
This testing follows the international standard ISO 7206-4, with manufacturers conducting sinusoidal compressive loading for 5 million cycles, equivalent to up ...
[95]
Fatigue Testing of Materials in a Corrosive Environment - TWI Global
TWI has specialist corrosion fatigue testing facilities which allow tests to be carried out in sour (H2S), sweet (CO2) and other corrosive environments.
[96]
Corrosion-Fatigue Failure of Gas-Turbine Blades in an Oil and ... - NIH
Failures of gas-turbine blades can be due to creep damage, high-temperature corrosion, high-temperature oxidation, fatigue, erosion, and foreign object damage ...
[97]
Crude Oil Corrosion Fatigue of L485MB Pipeline Steel
The aim of the investigation was to assess the degree of degradation of the fatigue properties of this steel due to the action of environments typical for crude ...
[98]
E466 Standard Practice for Conducting Force Controlled Constant ...
Jul 2, 2021 · 1.1 This practice covers the procedure for the performance of axial force controlled fatigue tests to obtain the fatigue strength of metallic ...
[99]
E739 Standard Practice for Statistical Analysis of Linear or ... - ASTM
Mar 1, 2023 · 4.1 Materials scientists and engineers are making increased use of statistical analyses in interpreting S-N and ε-N fatigue data.
[100]
ISO 13003:2003 - Fibre-reinforced plastics
In stock 2–5 day deliveryISO 13003:2003 defines the general procedures for fatigue testing of fibre-reinforced plastic composites under cyclic loading conditions.
[101]
De Havilland DH-106 Comet 1 | Federal Aviation Administration
Mar 7, 2023 · The squarish windows and window frames created high stress concentrations which were not detected during testing. The production aircraft fleet ...
[102]
Fatigue failure of the de Havilland comet I - ScienceDirect
The investigation explored a number of avenues, and finally gave structural failure of the pressure cabin brought about by fatigue as the cause of the accidents ...
[103]
[PDF] The Real Story of the Comet Disasters - HAW Hamburg
Jan 24, 2019 · First accident of a De Havilland Comet was on 10th January 1954. G ... □ De Havilland estimated stress would reach 190 MPa near cut.Missing: concentrations | Show results with:concentrations
[104]
Technical Problem Identification for the Failures of the Liberty Ships
The welds produced by largely unskilled work force contain crack type flaws. Beyond these cracks, another important reason for failure associated with welding ...Missing: fatigue imperfections
[105]
Revisiting (Some of) the Lasting Impacts of the Liberty Ships via a ...
Oct 26, 2015 · It was most common that the defects would arise from the welds associated with the bilge keels, where a bulb bar was used to form the keel. The ...Missing: fatigue imperfections
[106]
Liberty Ship - an overview | ScienceDirect Topics
In the case of the Liberty ships there were stress concentrations at the hatch corners, weld defects and fatigue cracks. The tiebars on the jacks of the Sea ...Missing: imperfections | Show results with:imperfections
[107]
[PDF] AAR-89-03 - NTSB
Jun 14, 1989 · AAR-89-03 reports Aloha Airlines Flight 243 experienced an explosive decompression and structural failure near Maui, Hawaii on April 28, 1988.
[108]
Boeing 737-200 | Federal Aviation Administration
Dec 19, 2022 · The Aloha Airlines 737-200 accident was caused by a failure to detect disbonding and fatigue damage in the fuselage lap splice, leading to a ...
[109]
Study of multi-site damage of fuselage lap joints - ScienceDirect
On 28 April 1988 Aloha Airlines Flight 243, a Boeing 737-200 was undertaking ... Fatigue testing of Boeing lap joint specimens. In this test program 10 ...
[110]
[PDF] Revisiting Aloha Airline Flight 243: Corrosion Engineer's Stand point
Aloha Airline Flight 243's story includes the catastrophe, damage details, airplane history, lap joint issues, maintenance record, metallurgical investigation, ...
[111]
Fatigue Testing of a Stiffened Lap Joint Curved Fuselage Structure
In April 1988, Aloha Airlines flight 243 experienced an explosive midair decompression that resulted in the separation of an 18-foot section of the fuselage ...
[112]
[PDF] Beyond the limits of imagination: what do the Comet aircraft failures ...
Another issue was the Comets' square-shaped windows, which only had small rounded corners. This shape generated stress concentrations at the windows' corners.
[113]
An Investigation of the Anisotropic Fatigue Properties of Laser ...
The LAM Ti-6Al-4V alloy exhibits obvious anisotropic fatigue properties and significant dispersion in fracture position.Missing: NASA lattice
[114]
Fatigue behaviour of diamond based Ti-6Al-4V lattice structures ...
The present study reported that the fatigue resistance of diamond based lattice structures produced by L-PBF in Ti-6Al-4V is strongly dependent on the load ...
[115]
Fatigue evaluation test method using the inertia generator for the ...
Jul 15, 2023 · Full-scale validation tests consist of several static extreme load, two consecutive cyclic fatigue, and post-fatigue static tests. The objective ...Missing: gusts | Show results with:gusts
[116]
Impact of vibrations on lithium-ion batteries in electric vehicles
This review investigated the impact of vibrations on EV batteries by drawing connections between vibration and battery performance, highlighting EV NVH sources,
[117]
[PDF] CLEAN SKY 2 ACHIEVEMENT REPORT
The Clean Sky 2 programme was successfully concluded in 2024, after 10 years of innovation and collaboration across Europe, achieving a number of milestones and ...Missing: AI fatigue
[118]
A Certifiable Machine Learning-Based Pipeline to Predict Fatigue ...
Sep 12, 2025 · In this paper, we present a ML-based pipeline that aims to estimate the fatigue life of different aircraft wing locations given the flight ...