Lithium titanate

Lithium titanates are a family of inorganic compounds containing lithium, titanium, and oxygen, including lithium metatitanate (Li₂TiO₃) used in nuclear applications and the spinel lithium titanate (Li₄Ti₅O₁₂), which is recognized for its role as a high-performance anode material in lithium-ion batteries.^[1] The spinel Li₄Ti₅O₁₂ features a three-dimensional defect spinel framework where lithium ions occupy both tetrahedral (8a) and octahedral (16d) sites, enabling reversible lithium intercalation to form Li₇Ti₅O₁₂ with negligible volume expansion of less than 0.1%, often referred to as a "zero-strain" insertion host.^[1] Key properties of Li₄Ti₅O₁₂ include a theoretical specific capacity of 175 mAh g⁻¹ and an operating voltage plateau around 1.55 V versus Li/Li⁺, which inherently suppresses solid electrolyte interphase (SEI) formation and mitigates risks associated with lithium dendrite growth.^[1] Despite its advantages in safety, thermal stability, and exceptional cycling performance—capable of enduring thousands of charge-discharge cycles at high rates—its electronic conductivity remains low at approximately 10⁻¹² to 10⁻¹³ S cm⁻¹, and ionic conductivity is around 3 × 10⁻¹⁰ S cm⁻¹, necessitating enhancements like nanostructuring, doping (e.g., with Al or Mg), or carbon coatings to improve rate capability.^[1] These modifications enable applications in fast-charging electric vehicles, grid-scale energy storage, and high-power micro-batteries, where Li₄Ti₅O₁₂'s stability outperforms traditional graphite anodes.^[2] Commercially, Li₄Ti₅O₁₂ has been integrated into lithium titanate batteries (LTBs) since the mid-2000s, powering applications like electric buses and uninterruptible power supplies due to its wide operating temperature range and abuse tolerance.^[1]

Chemical Composition and Properties

Lithium Metatitanate (Li₂TiO₃)

Lithium metatitanate, denoted by the chemical formula Li₂TiO₃, possesses a molar mass of 109.75 g/mol.^[3] This compound represents a key form of lithium titanate, distinguished by its ordered atomic arrangement involving lithium, titanium, and oxygen in a 2:1:3 stoichiometric ratio. At room temperature, β-Li₂TiO₃ crystallizes in a monoclinic structure with the C2/c space group, exhibiting a layered configuration of edge-sharing TiO₆ octahedra and LiO₆ octahedra that form alternating planes.^[4] This arrangement contributes to its distorted rock-salt-like framework, with lattice parameters approximately a = 5.062 Å, b = 8.788 Å, c = 9.753 Å, and β = 100.21°.^[4] The β-phase remains stable up to high temperatures, providing a robust structural basis for its applications. Upon heating, β-Li₂TiO₃ undergoes a reversible order-disorder phase transition to the cubic γ-Li₂TiO₃ phase above 1150–1250 °C, adopting a NaCl-type structure with a lattice parameter of about 4.15 Å.^[5] This transformation involves increased disorder in the cation sublattice, with the enthalpy change measured at approximately 11.8 kJ/mol near 1410 K.^[5] The γ-phase persists until melting and reverts to the β-phase upon cooling, highlighting the material's thermal reversibility. Li₂TiO₃ manifests as a white powder with a density of 3.43 g/cm³ and a melting point of 1533 °C.^[6] It demonstrates excellent chemical stability in air and notable resistance to hydration, attributes that enhance its suitability for demanding environments such as tritium breeding in nuclear fusion reactors.^[7]

Spinel Lithium Titanate (Li₄Ti₅O₁₂)

Spinel lithium titanate, denoted as Li_4Ti_5O_{12}, crystallizes in a cubic spinel structure with the space group Fd\bar{3}m, where lithium ions occupy tetrahedral 8a sites and titanium ions are distributed across octahedral 16d sites, forming a framework of face-sharing octahedra that supports reversible ion intercalation.^[8] This structural arrangement contributes to its exceptional electrochemical stability, making it a preferred material for advanced energy storage applications.^[9] A defining feature of Li_4Ti_5O_{12} is its "zero-strain" lithium insertion mechanism, whereby the phase transition from Li_4Ti_5O_{12} to Li_7Ti_5O_{12} during lithiation occurs with minimal volume change of approximately 0.2%, preserving the cubic lattice integrity and mitigating mechanical degradation over repeated cycling. This behavior arises from the solid-solution-like reaction at the 1.55 V plateau versus Li/Li^+, enabling a theoretical specific capacity of 175 mAh/g based on the intercalation of three lithium ions per formula unit. The flat voltage profile further enhances its suitability as a stable anode component in lithium-ion systems.^[9] Nanocrystalline variants of Li_4Ti_5O_{12}, typically with particle sizes below 100 nm, exhibit improved rate capability owing to shortened diffusion paths for lithium ions and enhanced electronic conductivity at grain boundaries, which can increase effective charge transfer by orders of magnitude compared to micron-sized counterparts.^[10] Particle size reduction from bulk to nanoscale domains thus optimizes kinetic performance without compromising the inherent structural advantages.^[11] Li_4Ti_5O_{12} demonstrates robust thermal stability, remaining structurally intact up to 600 °C under inert atmospheres, as evidenced by minimal weight loss or phase decomposition in thermal analysis up to higher temperatures.^[12] Additionally, it features low self-discharge rates, typically below 5% over extended storage periods, attributable to the absence of solid electrolyte interphase formation and high redox potential that suppresses parasitic reactions.^[13] Doping strategies, such as with aliovalent ions, can further enhance conductivity, though detailed implementations are addressed in synthesis discussions.^[14]

Other Lithium Titanates

Lithium orthotitanate, Li₄TiO₄, adopts an orthorhombic crystal structure in the Cmcm space group, featuring tetrahedrally coordinated Ti⁴⁺ ions within an approximately tetragonally packed oxide ion array.^[15] This compound exhibits lithium-ion conductivity, which can be enhanced through sulfur doping to achieve values suitable for solid-state applications.^[16] However, Li₄TiO₄ demonstrates limited thermal stability, undergoing lithium loss and partial decomposition at temperatures around 900°C, in contrast to the more robust metatitanates like Li₂TiO₃ that maintain integrity under similar conditions.^[17]^[18] Dilithium trititanate, Li₂Ti₃O₇, possesses a layered structure related to Na₂Ti₃O₇ in the monoclinic P2₁/m space group, characterized by an open framework that facilitates ion mobility.^[19] This architecture enables effective ion exchange, particularly for protons, making it relevant for selective ion separation processes.^[20] Lithium monotitanate, LiTiO₂, crystallizes in a rock-salt structure, serving as the fully lithiated end member of the LixTiO₂ series (0 ≤ x ≤ 1).^[21]

Synthesis Methods

Solid-State and Ceramic Processing

Solid-state reactions represent a conventional high-temperature method for synthesizing lithium titanate, particularly lithium metatitanate (Li₂TiO₃), suitable for bulk production in ceramic applications. This process typically involves mixing stoichiometric amounts of lithium carbonate (Li₂CO₃) and titanium dioxide (TiO₂) precursors, often in a ball mill to ensure homogeneity, followed by calcination at temperatures between 700°C and 900°C for several hours to initiate the reaction and form the desired phase. For spinel lithium titanate (Li₄Ti₅O₁₂), solid-state synthesis uses similar precursors (Li₂CO₃ and anatase TiO₂), with calcination typically at 800–900°C to achieve the spinel phase.^[22] The calcined powder is then pelletized or shaped and sintered at approximately 1,200°C to achieve densification and phase stability, yielding dense Li₂TiO₃ ceramics with controlled microstructure.^[23]^[24] Achieving phase purity in solid-state synthesis requires precise control of precursor stoichiometry, as deviations can lead to impurities such as residual TiO₂. Incorporating excess lithium in the initial mixture—typically 5–10 mol% beyond stoichiometry—compensates for potential losses and suppresses TiO₂ formation by promoting complete reaction to Li₂TiO₃, resulting in single-phase products verified by X-ray diffraction.^[25]^[26] For nuclear applications, such as tritium breeding materials, Li₂TiO₃ powders produced via solid-state routes are processed into pebbles through extrusion and subsequent sintering. The powder is mixed with a binder, extruded into cylindrical extrudates, spheronized to form spheres of 0.5–1 mm diameter, dried, and sintered at 900–1,100°C to attain densities of 80–90% theoretical while maintaining open porosity for gas permeation.^[27]^[28]^[29] Recent advances include cold sintering processes enabling densification below 300°C using transient liquid phases, as demonstrated in July 2025, which minimize energy consumption and lithium volatilization. Additionally, 3D printing combined with pressureless sintering at around 1200°C has been reported as of March 2025 for fabricating complex Li₂TiO₃ structures with improved dielectric properties.^[30]^[31] Despite its scalability, solid-state and ceramic processing of lithium titanates is energy-intensive due to the prolonged high-temperature steps required for reaction and densification. A notable drawback is lithium volatilization as Li₂O or other species above 1,000°C, which can alter composition, reduce yield, and necessitate excess precursors, thereby increasing material costs and environmental impact.^[31]^[32]

Solution-Based Techniques

Solution-based techniques for synthesizing lithium titanates encompass wet chemistry approaches that enable precise control over particle morphology and size, particularly for nanoscale materials suitable for energy storage and nuclear applications. These methods typically involve the dissolution of precursors in solvents, followed by reactions such as hydrolysis or precipitation, and subsequent thermal treatment at moderate temperatures to form the desired phases. Unlike high-temperature solid-state routes, solution-based processes facilitate homogeneous mixing at the molecular level, leading to uniform nanostructures with reduced defects.^[33] The sol-gel process is a prominent method for producing spinel lithium titanate (Li₄Ti₅O₁₂), starting with the hydrolysis of titanium alkoxides, such as titanium isopropoxide or tetra-n-butoxide, in the presence of lithium salts like lithium acetate or nitrate. During this process, the alkoxide undergoes hydrolysis to form a sol, which then condenses into a gel network incorporating lithium ions; the gel is dried and calcined at temperatures between 500 and 800 °C to yield crystalline Li₄Ti₅O₁₂ nanoparticles. This approach results in particles typically in the 10–50 nm range, offering high surface area and improved ion diffusion pathways compared to bulk materials.^[34]^[35] Hydrothermal synthesis is particularly effective for lithium metatitanate (Li₂TiO₃), involving aqueous reactions of titanium sources, such as anatase TiO₂ or titanium dioxide xerogel, with lithium hydroxide under autogenous pressure at 150–250 °C for several hours. This pressurized environment promotes the formation of uniform nanocrystals with monoclinic structure, often requiring post-annealing at around 600–700 °C to enhance crystallinity while preserving nanoscale dimensions of 20–100 nm. The method's aqueous nature ensures eco-friendly processing and high phase purity, making it ideal for tritium breeding ceramics.^[36]^[37] Doping with elements like niobium (Nb) or aluminum (Al) can be readily incorporated during solution-based synthesis to improve electronic conductivity in Li₄Ti₅O₁₂. In sol-gel routes, niobium precursors such as niobium ethoxide are added to the titanium-lithium sol, followed by calcination, yielding compositions like Li₄Ti₄.₉₅Nb₀.₀₅O₁₂ that exhibit enhanced rate capability due to increased electrical conductivity from Nb⁵⁺ substitution on Ti⁴⁺ sites. Similarly, aluminum doping via aluminum nitrate in the sol-gel mixture produces Al-substituted LTO (e.g., Li₄Ti₄.₉₅Al₀.₀₅O₁₂), which stabilizes the spinel structure and boosts lithium-ion diffusion. Hydrothermal methods also support doping by co-precipitating metal salts, allowing tailored electronic properties without compromising nanoscale morphology.^[38]^[39] These techniques offer key advantages, including lower processing temperatures that minimize lithium volatilization and phase impurities, as well as the production of nanoscale products (10–100 nm) with superior uniformity and reactivity. Such features enhance the materials' performance in applications requiring high surface area, while enabling easier integration of dopants for property optimization.^[33]^[36]

Applications in Energy Storage

Anode in Lithium-Ion Batteries

Lithium titanate, specifically the spinel phase Li₄Ti₅O₁₂ (LTO), serves as a promising anode material in lithium-ion batteries, replacing traditional graphite anodes to enhance safety and longevity in applications requiring high power and rapid charging.^[2] This substitution leverages LTO's spinel structure, which enables zero-strain insertion of lithium ions during charge-discharge cycles, minimizing mechanical degradation.^[40] When paired with cathodes such as LiFePO₄ or nickel-manganese-cobalt (NMC) oxides, LTO-based cells achieve a nominal operating voltage of approximately 1.9 V with LiFePO₄ and 2.2–2.4 V with NMC, suitable for energy storage systems in electric vehicles and grid applications.^[41]^[42] LTO anodes demonstrate exceptional cycle life, often exceeding 10,000 cycles at high rates up to 10C, with capacity retention greater than 90%.^[43] This durability stems from the material's structural stability and fast lithium-ion diffusion kinetics, allowing sustained performance under demanding conditions like frequent fast charging.^[44] Key safety advantages of LTO anodes include the absence of a solid electrolyte interphase (SEI) layer formation, as lithium intercalation occurs at a potential above 1.5 V versus Li/Li⁺, preventing electrolyte decomposition and lithium plating.^[45] This feature, combined with the material's wide operational temperature range from -50 °C to 60 °C, reduces risks associated with thermal runaway, making LTO suitable for harsh environments where graphite anodes fail.^[46] Furthermore, the lack of SEI and zero-strain behavior contributes to lower heat generation during operation, enhancing overall battery safety compared to conventional systems.^[47] Despite these benefits, LTO anodes involve energy density trade-offs, with full cells typically achieving 60–80 Wh/kg, significantly lower than the 150+ Wh/kg of graphite-based counterparts due to LTO's higher intercalation voltage and lower specific capacity.^[48] This limitation arises from the thermodynamic profile of lithium insertion in LTO, prioritizing power over energy storage.^[40] Recent advancements in 2025 have focused on hybrid LTO-graphene composites to address LTO's inherently low electronic conductivity, improving rate capability and overall performance through enhanced electron transport pathways.^[49] These composites integrate graphene's high conductivity with LTO's stability, enabling better electrochemical kinetics in high-power applications.^[50]

Cathode in Fuel Cells and Batteries

Lithium metatitanate (Li₂TiO₃) functions as a stable cathode support material in molten carbonate fuel cells (MCFCs), where it is combined with lithiated nickel oxide (NiO) to form a protective layer that enhances durability under high-temperature operation at approximately 650 °C. This configuration facilitates efficient CO₂ transport to the cathode-electrolyte interface, enabling the reduction of CO₂ and O₂ to carbonate ions (CO₃²⁻) that migrate through the molten electrolyte. The transformation of TiO₂ coatings into Li₂TiO₃ during exposure to the carbonate melt (e.g., Li₂CO₃-K₂CO₃ eutectic) creates a barrier that reduces Ni dissolution by up to 50% compared to uncoated cathodes, thereby mitigating performance degradation over extended operation (up to 230 hours).^[51] The material's chemical stability in aggressive carbonate melts and resistance to sintering at elevated temperatures contribute to its suitability, preventing structural collapse and maintaining porous architecture for gas diffusion. In MCFC prototypes incorporating such supported cathodes, power densities of up to 150 mW/cm² have been reported under standard operating conditions (e.g., 140–160 mA/cm² at 0.7–0.9 V per cell). However, Li₂TiO₃ exhibits inherently low electronic conductivity (on the order of 10⁻¹¹ S/cm), which can limit overall cell performance; this is often addressed through co-doping with transition metals like Fe or Co to enhance charge transport while preserving ionic pathways.^[51]^[52]^[53]

Applications in Nuclear Technology

Tritium Breeding Materials

Lithium metatitanate (Li₂TiO₃) serves as a promising solid tritium breeder material in fusion reactor blankets due to its favorable thermochemical stability and lithium density, enabling the nuclear reaction ^6\mathrm{Li} + n \rightarrow ^4\mathrm{He} + \mathrm{T}, where T denotes tritium.^[54] To achieve a high tritium breeding ratio (TBR) of 1.1–1.2, essential for self-sustaining fusion operations, Li₂TiO₃ is typically enriched to 90% in ^6\mathrm{Li}, optimizing neutron capture efficiency while minimizing unwanted ^7\mathrm{Li} interactions.^[55] This enrichment enhances the exothermic reaction's yield, contributing up to 4.78 MeV per event, which supports overall blanket energy multiplication.^[56] In designs for major fusion projects like ITER and DEMO reactors, Li₂TiO₃ is fabricated into pebble beds within the breeding blanket to facilitate heat transfer and tritium extraction. These beds consist of spherical pebbles measuring 0.5–1 mm in diameter, packed to approximately 80% of theoretical density, allowing for void spaces that accommodate purge gas flow and mitigate thermomechanical stresses.^[29] The pebble geometry promotes uniform neutron irradiation and structural resilience, with the blanket configuration integrating beryllium multipliers to boost the TBR beyond unity. Such setups are critical for maintaining operational efficiency under high neutron loads. Tritium release from irradiated Li₂TiO₃ follows a diffusion-controlled mechanism, predominant at operating temperatures of 500–800 °C, where bred tritium migrates through the ceramic lattice as tritiated species like HT or T₂.^[57] A helium purge gas containing 3% hydrogen (He + 3% H₂) sweeps through the pebble bed to extract and convert surface-bound tritium, enhancing recovery rates by promoting isotope exchange and reducing retention. This process ensures low tritium inventory, typically below 1 g per module, vital for safety and fuel cycle efficiency.^[58] Under fusion-relevant conditions, Li₂TiO₃ demonstrates robust radiation stability, retaining mechanical integrity and phase purity when exposed to 14 MeV neutron fluxes up to 3 MW/m², as projected for DEMO-class reactors. Post-irradiation analyses reveal minimal degradation in density or crush strength, even after displacements per atom (dpa) levels exceeding 100, attributable to the material's low swelling and resistance to amorphization.^[29] Recent advancements as of 2025 include ongoing tests in the IFMIF-DONES facility, evaluating enhanced breeding performance through high-fidelity neutron irradiation of Li₂TiO₃ pebbles to validate TBR predictions and tritium release kinetics under prototypic conditions.^[59]

Breeder Material Synthesis and Processing

The fabrication of Li₂TiO₃ pebbles for tritium breeding applications often employs the extrusion-spheroidization-sintering process to achieve the required spherical morphology and mechanical integrity. This method involves mixing Li₂TiO₃ powder with organic binders such as polyvinyl alcohol to form a paste, followed by extrusion through a die to produce cylindrical extrudates, which are then rounded into spheres via a spheronizer operating at controlled speeds. The green pebbles are subsequently dried and sintered at approximately 1,100 °C in air for several hours to densify the structure while minimizing phase impurities, resulting in pebbles with diameters of 0.5–1 mm and crush strengths exceeding 30 N, essential for withstanding blanket pressures.^[60]^[27] To enhance tritium release kinetics and mechanical durability, Li₂TiO₃ is commonly doped with 5–10 wt% TiO₂, which stabilizes the microstructure and increases crush strength by up to 1.5 times compared to undoped variants, as demonstrated in studies for ITER test blanket modules. The added TiO₂ promotes finer grain sizes (<5 μm) and reduces sintering shrinkage, optimizing purge gas interaction for efficient tritium extraction without compromising breeding performance.^[61]^[62] Quality control in processing focuses on achieving 5–15% open porosity to facilitate helium purge gas permeation and tritium diffusion, while maintaining overall density above 80% of theoretical to ensure structural integrity. Techniques such as controlled sintering atmospheres and Li-rich precursors (Li/Ti ratio >2) are employed to prevent lithium volatilization, which can occur above 900 °C and lead to phase decomposition; post-sintering characterization via mercury porosimetry and helium pycnometry verifies uniformity.^[29]^[63] Scaling production to kilogram batches poses challenges, particularly in maintaining uniform ⁶Li enrichment levels of 90% required for high breeding ratios in DEMO reactors, due to the high cost and limited supply of enriched lithium precursors. Inhomogeneities in enrichment during mixing and sintering can reduce tritium yield, necessitating advanced isotopic analysis and batch-wise processing to achieve consistency across large volumes.^[64]^[65] Recent advancements include the melt-spray technique, which involves melting Li₂TiO₃ at 1,400–1,500 °C and spraying droplets into a cooling medium to form denser pebbles (up to 90% theoretical density) with improved sphericity, tested in 2024–2025 European fusion programs under EUROfusion for enhanced scalability and tritium retention.^[66]^[67]

Other Industrial Applications

Sintering Aids in Ceramics

Lithium titanate, specifically Li₂TiO₃, is used as a flux in porcelain enamels and ceramic insulating bodies based on titanates due to its chemical stability.^[68] In the Li₂O-TiO₂ system, Li₂TiO₃ is a stable phase that forms solid solutions extending from approximately 44 to 66 mol% TiO₂ and exhibits an order-disorder transition at 1,215 °C.^[69] The system's stable phases include Li₄TiO₄, Li₂TiO₃, Li₄Ti₅O₁₂, and Li₂Ti₃O₇. Li₂TiO₃-based ceramics have been explored for low-temperature co-fired ceramic (LTCC) applications in microwave dielectrics, often with additives like LiF to lower sintering temperatures.^[70]

Role in Crystallization Processes

In the Li₂O-TiO₂ system, phase diagram studies indicate that Li₂TiO₃ forms as a primary phase, contributing to predictable crystallization paths during thermal processing of titanate materials.^[69]

References

[1]
Lithium Titanate (li4ti5o12) - an overview | ScienceDirect Topics
Lithium titanate (Li4Ti5O12) is a defect spinel anode with high power, thermal stability, and zero strain, allowing lithium intercalation without volume change ...
[2]
A review of spinel lithium titanate (Li4Ti5O12) as electrode material ...
Spinel Li 4 Ti 5 O 12 is a promising the state-of-the-art anode material because of its outstanding safety, excellent cycling stability, and stable charge/ ...
[3]
Lithium titanium oxide (Li2TiO3) | Li2O3Ti | CID 160968 - PubChem
Synonyms. Lithium titanium oxide (Li2TiO3); Titanate (TiO32-), dilithium; EINECS 234-759-6; RefChem:153771; 12031-82-2 ; Molecular Weight. 109.8 g/mol. Computed ...
[4]
Influence of Lithium Vacancy Defects on Tritium Diffusion in β-Li2TiO3
May 13, 2020 · ... γ-phases are present at temperatures above and below this range, respectively. ... Li2TiO3 undergoes an order-disorder phase transition at 1215°.<|separator|>
[5]
Enthalpy, heat capacity and enthalpy of transformation of Li 2 TiO 3
The high-temperature γ-Li2TiO3 phase is cubic and crystallises in the NaCl type structure, Z=4/3, with the room temperature lattice parameter a=415.05 pm.
[6]
https://www.msesupplies.com/products/mse-pro-lithium-titanate-li-sub-2-sub-tio-sub-3-sub-powder-99-2n
[7]
[PDF] INVESTIGATIONS OF LITHIUM CARBIDE AS TRITIUM BREEDING ...
Lithium metatitanate (Li2TiO3) attracts attention due to its chemical stability and high rate of tritium release at ... activation, resistance to hydration, and ...
[8]
Synthesis and characterization of spinel Li4Ti5O12 anode material ...
... spinel structure (Fd3m space group) have been obtained at 800 °C for 16 h. SEM analyses indicated that the prepared Li4Ti5O12 powders had a uniform cubic ...
[9]
Two-Dimensional Wavelike Spinel Lithium Titanate for Fast ... - Nature
May 18, 2015 · All Bragg peaks of the obtained samples are consistent with those of spinel Li4Ti5O12 phase (space group Fd3m (227), JCPDS no. 049-0207) ...
[10]
Size Effects in the Li4+xTi5O12 Spinel - ACS Publications
Nov 17, 2009 · The nanosized Li4+xTi5O12 spinel is investigated by electrochemical (dis)charging and neutron diffraction. The near-surface environment of ...
[11]
https://www.electrochemsci.org/papers/vol9/90401583.pdf
[12]
Thermal reactivity study of spinel lithium titanium oxide material for ...
This paper reports the study on thermal reactivity of spinel lithium titanium oxide (Li4Ti5O12) material. Thermalgravimetry and Differential scanning ...
[13]
12 V-Class Bipolar Lithium-Ion Batteries Using Li4Ti5O12 Anode for ...
Dec 14, 2016 · The LMFP cathode had excellent cycle life performance during high-temperature cycling at 60°C and over-discharge cycling tests. In the case of ...
[14]
Doubling Reversible Capacities in Epitaxial Li4Ti5O12 Thin Film ...
Apr 22, 2019 · (3−6) LTO is a lithium intercalation compound exhibiting a theoretical capacity of 175 mAh·g–1 with a flat insertion/extraction voltage of ...
[15]
Crystal Structure Refinement of Li4TiO4 Containing Tetrahedrally ...
It is isostructural with Li4GeO4 and contains tetrahedrally coordinated Ti4+ ions and an approximately tetragonally packed oxide ion array.
[16]
New Li+-ion conductors, Li4 – 2Ti1 –SO4, based on the Li4TiO4 ...
The enhancement in conductivity is associated with an increase in concentration of lithium-ion vacancies, created via the mechanism 2Li++ Ti4+⇌ S6+, but is ...
[17]
Long‐term thermal stability of Li4TiO4–Li2TiO3 core–shell breeding ...
Mar 17, 2023 · The results show that this core–shell material loses 3.4% Li mass after heating for 30 days, resulting in a reduction in Li density to .415 g/cm 3.
[18]
First-principles calculation of the structural, electronic, dynamical ...
Li4TiO4 is thermodynamically stable at temperatures up to at least 950 °C and has a lithium density of 0.51 g/cm3, which is higher than most of the tritium ...
[19]
Synthesis, structure, and electrochemical Li-ion intercalation ...
Jan 31, 2008 · Li2Ti3O7 with the Na2Ti3O7-type layered structure was prepared from Na2Ti3O7 as a parent compound via ion exchange in molten LiNO3/LiCl at ...Missing: trititanate | Show results with:trititanate
[20]
Insight into Ramsdellite Li2Ti3O7 and Its Proton-Exchange Derivative
Jul 10, 2009 · Thus, it seems that water molecules enter the tunnels in the structure providing a vehicle mechanism for proton diffusion. ... Ion-Exchange ...
[21]
Preparation and Characterization of Rock Salt-type LiTiO 2
The results show that rock salttype LiTiO2 prepared by this method is a nanosized nonstoichiometric compound. Its crystal form is stable at annealing ...
[22]
Rock Salt-Type LiTiO 2 @LiNi 0.5 Co 0.2 Mn 0.3 O 2 as Cathode ...
Aug 27, 2019 · Therefore, the core–shell structure of the cathode material is stable, and LiTiO2 with its three-dimensional lithium-ion diffusion path can ...
[23]
Synthesis of Li 2 TiO 3 by sol–gel combustion method and its gel ...
Conventionally, Li2TiO3 was prepared by solid state reaction using mixture of Li2CO3 and TiO2 as precursors at 750–800 °C temperature for 5–10 h duration [11–14] ...
[24]
Solid-state synthesis of submicron-sized Li4Ti5O12/Li2TiO3 ...
Aug 10, 2025 · TiO2 (anatase, AR) and Li2CO3 (industrial grade) were mixed thoroughly and sintered in a tube furnace at 750 ℃ in the air for 12 h. ... ... To ...
[25]
Synthesis & fabrication of lithium-titanate pebbles for ITER breeding ...
A process has been developed based on the solid state reaction of lithium-carbonate and titanium-dioxide for the synthesis of lithium titanate and pebble ...
[26]
A comparative study on the properties of Li 2 TiO 3 powders and ...
Jan 10, 2023 · When the sintering temperature is 1100°C, the pores disappear rapidly and the grain size grew abnormally to 12.9 μm. While the crushing load and ...
[27]
Transport and Electrochemical Properties of Li4Ti5O12-Li2TiO3 and ...
Sep 1, 2022 · The low conductivity values can be explained by the absence of vacancies in positions 8a and interstitial lithium ions in positions 16c of the ...
[28]
[PDF] 1 Memory Effect on the Synthesis of Perovskite-Type Li-Ion ... - OSTI
Li2TiO3 synthesis Stoichiometric amounts of Li2CO3 and TiO2 were mixed using an agate mortar and pestle and heated in an alumina crucible to 1000 °C with a ...
[29]
Fabrication of Li 2TiO 3 pebbles by the extrusion–spheronisation ...
Aug 6, 2025 · Li2TiO3 pebbles are a ceramic breeder material option for the helium cooled pebble bed (HCPB) blanket being developed in the EU.
[30]
Fabrication of the Li2TiO3 tritium breeder pebbles by a capillary ...
Li2TiO3 is one of the most promising candidates among tritium breeders. In this work, Li2TiO3 pebbles with a narrow size distribution, high density, small grain ...
[31]
Recent Progress in Research of Solid Tritium Breeder Materials Li 2 ...
This paper aims to provide a systematic review of the current progress in Li 2 TiO 3 preparation methods as well as the high Li density, tritium release ...
[32]
3D printing and pressureless sintering of Li2TiO3 for next generation ...
Mar 12, 2025 · Others have ascribed poor sinterability of pure Li2TiO3 above 1000 °C to volatilization of Li2O, but the addition of 2.5 wt% ZnO–B2O3 frit and ...
[33]
Fabrication of Li4Ti5O12 (LTO) as Anode Material for Li-Ion Batteries
LTO has higher lithium intercalation potential, avoids dendrite growth, is zero-strain, and has a larger diffusion coefficient, but lower energy density and ...
[34]
Sol-Gel Synthesis of Nanocrystalline Mesoporous Li 4 Ti 5 O 12 Thin ...
Jul 14, 2020 · The development of anodes based on Li4Ti5O12 (LTO) for lithium ... However, lithium titanate, Li4Ti5O12 (LTO), is a promising candidate ...
[35]
Synthesis and characterization of Li 4 Ti 5 O 12 - ScienceDirect.com
Lithium titanate, Li4Ti5O12 was prepared by the sol–gel method. The precursor was sintered at various temperatures (700, 800, 900 and 1000 °C) for 1 h and ...<|control11|><|separator|>
[36]
(PDF) Synthesis of Lithium Titanium Oxide (Li4Ti5O12) through Sol ...
Jul 1, 2022 · Synthesis of Lithium Titanium Oxide (Li4Ti5O12) through Sol-Gel Method and the Effect of Graphene Addition in Lithium-Ion Battery Anodes. Trans ...
[37]
Hydrothermal Synthesis of Lithium Meta Titanate Nanocrystallites
Lithium meta titanate (Li2TiO3) is one of the most promising tritium breeding candidate materials. In this study, the nanocrystallites lithium-titanate with ...
[38]
Hydrothermal Synthesis of Lithium Meta Titanate Nanocrystallites
The results showed that the monoclinic phase of Li2TiO3 nanostructure with high purity can be synthesized by further heat treatment of the hydrothermal ...
[39]
Effect of Nb-doping on electrochemical stability of Li 4 Ti 5 O 12 ...
Aug 6, 2025 · Li4Ti4.95Nb0.05O12 is synthesized by a citric acid-assistant sol–gel method. X-ray diffraction (XRD) reveals that highly crystalline ...
[40]
Synthesis and Characterization of Al-Doped Li4Ti5O12 with Sol Gel ...
Spinel Li4Ti(5-x)O12Alx(x = 0, 0.05) was synthesized via sol gel method. The samples were sintered at 800 oC for 4 hours. The characterization of material ...
[41]
Review article Lithium titanate batteries for sustainable energy storage
This review covers Lithium titanate (Li4Ti5O12, LTO) battery research from a comprehensive vantage point. This includes electrochemical properties, ...
[42]
Co/S co-doped Li4Ti5O12 as lithium-ion batteries anode for high-rate
Dec 20, 2023 · ... cycle life [[16], [17], [18]]. Ion doping can increase the intrinsic ... 10,000 cycles at 10C), exceptional cycling performance, stable ...
[43]
[PDF] Degradation of commercial Li4Ti5O12-based lithium-ion ... - MIT
Feb 27, 2025 · Li4Ti5O12 (LTO) is a promising anode material for lithium-ion batteries (LIBs) due to its good cycle stability, rate capability, and safety.
[44]
Two-dimensional graphene-based Li4Ti5O12 with hierarchical pore ...
Feb 10, 2022 · ... cycle performance with a capacity retention of 93.4 % over 10,000 cycles. When configurated with LiFePO4 cathode, the lithium ion full cell ...
[45]
Role of Electrolytes in the Stability and Safety of Lithium Titanate ...
It has been shown that LTO electrodes with carbon coatings can show resistance to gas formation and ensure higher stability for the battery. The electrolyte ...
[46]
Guide to anode materials in lithium-ion batteries
Dec 16, 2024 · Operating temperature range: -40°C to 60°C. Verified cycle life exceeding 10,000 cycles. Fast charging capability achieving 80% in 3-10 minutes.
[47]
Perspective Chapter: Thermal Runaway in Lithium-Ion Batteries
An LTO anode does not need an SEI layer, making it safer. However, the ... Lithium-ion Battery Safety Issues for Electric and Plug-in Hybrid Vehicles (Report No.
[48]
What is an LTO Battery? - Ossila
This results in a lower energy density (~70-100 Wh/kg) for LTO-based batteries compared to standard lithium-ion batteries with graphite anodes (~150-250 Wh/kg).
[49]
Modeling the Quantum Capacitance of 2D Graphene, LVP, and LTO ...
Oct 27, 2025 · The main drawbacks of LTO include its low electronic conductivity, while LVP suffers from a limited cycling lifespan. Carbon nanostructures are ...
[50]
Modeling the Quantum Capacitance of 2D Graphene, LVP, and LTO ...
Nov 1, 2025 · Modeling the Quantum Capacitance of 2D Graphene, LVP, and LTO Composite Films with Evolving Composition During (De)lithiation. October 2025 ...
[51]
[PDF] Adequacy of new electrolyte compositions and nanostructured ...
Oct 24, 2017 · cathode of molten carbonate fuel cells. Abstract: In this work, we develop two major research routes related to molten carbonates. The first ...<|control11|><|separator|>
[52]
[PDF] International Status of Molten Carbonate Fuel Cell (MCFC ...
The typical nominal current density of MCFC is 140-160 mA cm-2 at about 0.7 volt. The actual operating current density depends on a number of factors, ...
[53]
Electrical conductivity of Li 2TiO 3 ceramics - ResearchGate
Aug 7, 2025 · However, β-Li2TiO3 is a wide gap semiconductor with an indirect band gap at Γ-C (Eg ≈ 3.9 eV) with low electrical conductivity of 10 −11 S cm −1 ...
[54]
Defect process and lithium diffusion in Li2TiO3 - ScienceDirect.com
Dec 1, 2018 · Li2TiO3 is considered as a cathode material in batteries and in that respect it is important to investigate its defect processes and in ...
[55]
Synthesis & fabrication of lithium-titanate pebbles for ITER breeding ...
Aug 10, 2025 · 6Li produces tritium by (n, α) nuclear reaction, 6Li+1n→4He+3H. Lithium titanate (Li2TiO3) enriched with 6Li, is the most promising ...
[56]
[PDF] Tritium Breeding Ratio Evaluation of Solid Breeder Concepts for the ...
All cases were modeled using natural Li and 90% enriched Li-6, both as a start. A parametric study was performed for cases involving breeders and neutron ...
[57]
[PDF] Optimization of Tritium Breeding Ratio in a DT and DD Submersion ...
Sep 30, 2023 · The breeder blanket can augment the incident energy via exothermic reactions including the 6Li(n, t)4He reaction which has a Q value of 4.79MeV.
[58]
Tritium release performance of neutron-irradiated core–shell Li 2 TiO 3
To explore the tritium release mechanisms, we employed diffusion-controlled kinetics for curve fitting the isothermal tritium release spectrum at various ...
[59]
Effects of helium and ambient water vapor on tritium release from ...
Aug 6, 2025 · Isotope exchange processes with water vapor in purge gas enhanced the recovery of tritium adsorbed on the surface of Li2TiO3 and trapped in ...
[60]
Breeding blanket mock-up testing in IFMIF-DONES - IOPscience
Sep 30, 2025 · The main objective of the TRTM was to enable in-situ monitoring of tritium release from lithium ceramics and beryllium pebble beds during ...Missing: Li2TiO3 | Show results with:Li2TiO3
[61]
Li 2 TiO 3 composite ceramic pebbles using extrusion and ...
The composite pebbles were fabricated using a cost-effective and simple technique called extrusion-spherodization. The sintered pebbles were characterized for ...Missing: spheroidization | Show results with:spheroidization
[62]
[PDF] FT/P1-09 Development of Advanced Blanket Materials for Solid ...
The collapse strength of 5mol% TiO2-doped Li2TiO3 pebbles was 1.5 times as large as that of un- doped Li2TiO3 pebbles. From these results, bright prospect ...
[63]
[PDF] JAERI-Review 2003-011 JP0350429 FT/Pl-09 1.23 Development of ...
Therefore, the development of TiO2- doped Li2TiO i started as improved tritium breeder. In this study, the characteristics of this material are compared to that ...
[64]
Fabrication of fine-grained Li 2 TiO 3 ceramic pebbles with ...
Li2TiO3 ceramic pebbles ought to have high crush strength and uniform microstructure for safety operation and efficient tritium release.
[65]
Development of methods for reprocessing and reuse of tritium breeder materials in broader approach activities
### Summary of Scale-Up Challenges for Li₂TiO₃ Production
[66]
U.K. Atomic Energy Authority Confirms Lithium Enrichment Challenge
Dec 28, 2023 · Lithium enrichment at scale would be required to breed the tritium fuel that will be needed for commercial deuterium-tritium fusion reactors.
[67]
A novel mass production method for Li2TiO3 tritium breeder ceramic ...
The melt spraying [20][21][22] and rolling ball [23, 24] methods are considered to be the methods for mass production of ceramic pebbles. However, most of ...
[68]
Tritium release performance of centrifugally granulated Li2TiO3 ...
Oct 7, 2025 · We show the results concerning Li2TiO3 pebbles bed specimens developed in the frame of the European fusion technology program. Read more.
[69]
Lithium Titanate (Li2TiO3) UK Supplier - Thermograde
Thermograde is a leading UK supplier of Lithium Titanate (Li2TiO3). Lithium Titanate is generally preferred as a flux due to its stable properties.
[70]
Phase equilibria in the system Li 2 O-TiO 2 - ScienceDirect.com
The system Li2O-TiO2 contains four stable phases: Li4TiO4, Li2TiO3, Li4Ti5O12 and Li2Ti3O7, and one metastable phase, H. Li2TiO3 undergoes an order-disorder ...
[71]
Lithium Titanate - Inter-China Chemical
Its chemical formulae is Li2TiO3 and features a layered crystal structure where lithium ions are interposed between titanium and oxygen atoms.Missing: Li₂TiO₃ mass phase transition
[72]
https://ceramics.onlinelibrary.wiley.com/doi/10.1111/jace.20573
[73]
Calcination of Metatitanic Acid to Titanium Dioxide White Pigments
Aug 9, 2025 · ... seed crystal ... The reduction in calcination temperature greatly alleviates the sintering tendency of TiO2 and aid to produce TiO2 crystals of ...
[74]
The effect of TiO2 on nucleation and crystallization of a Li2O ... - NIH
Feb 13, 2018 · Thus, it is shown that the nucleation of nanocrystalline TiO2 is initiated by a gradual re-arrangement of the Ti ions in the amorphous, glassy ...Missing: eutectic 1200-1400
[75]
(PDF) Investigation of Li2O and TiO2 effects on MAS glass-ceramic ...
Aug 6, 2025 · The results revealed that the addition of Li2O significantly reduced the crystallization activation energy of glass. Besides, as the Li2O ...
[76]
Machinability of lithium disilicate glass ceramic in in vitro dental ...
A machinability study has been made in the simulated oral clinical machining of LDGC with a dental handpiece and diamond burs.